在镀上金属电极前,对CdTe表面进行化学蚀刻是制备高效率碲化镉薄膜太阳电池的关键技术之一.本实验用Br2-甲醇对热处理后的CdTe薄膜进行蚀刻,并利用XRD、AFM研究其结构、成分和形貌.结果表明:蚀刻后的CdTe薄膜获得一银灰色的光洁表面,并发现CdTe薄膜表面产生一富Te层,蚀刻厚度达到1μm获得性能最好的太阳电池.用Br2-甲醇蚀刻后的CdTe薄膜,采用ZnTe/ZdTe:Cu复合层作为背接触层的过度层,已获得了转换效率为13.38%的太阳电池.
参考文献
| [1] | PowellRC;Sasala R A;Dover G et al.Development of thin-film CdTe phovoltaics[Z].Technical Digest of International PVSEC-9Miyazaki Japan,1996. |
| [2] | AramotoT;Ku mazawa S;Higuchi H et al.160%efficientthinfilmCdS/CdTesolarcells[J].Journal of Applied Physics,1997,36(10):6304-6305. |
| [3] | VllalHS;Zweibel K;Von Roedern B.Current status of polycrystalline thin-film PV technologies[A].New York,USA,IEEE,1997:301-305. |
| [4] | K Durose;M Burgelman .[J].Journal of Applied Physiology,1993,73:8381. |
| [5] | J P Ⅱaring;J G Werthen;R Bube.[J].Journal of Vacuum Science and Technology A-Vacuum Surfaces and Films,1983:1469. |
| [6] | SarlundJ;Ritala M;Leskela M et al.CharacterizationofEtchingProparationofCdTesolarcells[J].Solar Energy Materials and Solar Cells,1966,44:177-190. |
| [7] | D W Nikles;X Li;P Sheldon et al.[J].Journal of Applied Physiology,1995,77 |
| [8] | 黎兵,蔡亚平,朱居木,郑家贵,蔡伟,冯良桓.CdS多晶薄膜的制备及其性能的研究[J].四川大学学报（自然科学版）,1999(03):497. |
| [9] | 黄小融,郑家贵,蔡伟.CdS多晶薄膜的电学性质[J].半导体光电,1998(06):404-406,411. |
| [10] | 蔡伟,冯良桓,蔡亚平,张静全,武莉莉.CdTe薄膜的制备和后处理研究[J].四川大学学报(自然科学版),2002(02):273-276. |
| [11] | Picos-VegaA;Becerricl M;Zelaya-Angelo .[J].Journal of Applied Physiology,1998,83:760-763. |
| [12] | D. Ⅱ .Levi;L.M.Weods;D.S.Alin.[A].,1998:1047. |
| [13] | MORRISGC;TANNERPG .[J].Journal of Crystal Growth,1992,117:929. |
| [14] | MORRISGC;TOTTSZER A;DAS SK .[J].Materials Forum,1991,15:164. |
| [15] | FVLOPG;DOTY M;MYERS P et al.[J].Applied Physics Letters,1982,40:327. |
| [16] | 刘恩科;朱秉升;罗晋生.半导体物理学[M].北京:国防工业出版社,1994:193. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%