以Zr、Ti、Cu和C元素粉末为原料,用XRD、EPMA、SEM、力学性能检测等方法,研究机械合金化合成的ZrC/C和(ZrC+FiC)/Cu复合材料的力学和电学性能.实验结果表明:可以用机械合金化合成TiC、ZrC粉末.力学性能方面,经ZrC弥散的Cu基复合材料抗拉强度为359.45MPa,布氏硬度为146.2,经(ZrC+TiC)弥散的复合材料抗拉强度为377.3MPa,布氏硬度为166.5,说明ZrC作为第二相可以明显改善Cu基材料的力学性能,而且(ZrC+TiC)两相强化效果更好.由断口形貌分析,复合材料主要发生沿界面脆性断裂.电学性能方面,由于致密度不够高以及其他杂质相的引入,材料的相对电导率(IACS标准)有待提高.
参考文献
| [1] | 曾汉民.高技术新材料要览[M].北京:中国科学技术出版社,1993 |
| [2] | Jongsang Lee;J. Y. Jung;Eon Sik Lee;W. J. Park;S. Ahn;Nack J. Kim .Microstructure and properties of titanium boride dispersed Cu alloys fabricated by spray forming[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):274-283. |
| [3] | 张树玉,闵光辉,于化顺.原位反应TiB2／Cu-Zr复合材料的力学与电学性能[J].功能材料,2000(03):269. |
| [4] | T J Miller;S J Zinkle;B A Chin .Strength and fatigue of dispersion-strengthened copper[J].Journal of Nuclear Materials,1991,179:263-266. |
| [5] | Besterci Michal;Ivan Jozef;Kovac Ladislav .Influence of particles in Cu-Al2O3 system on fracture mechanism[J].Materials Science and Engineering A,2001,319-321:667-670. |
| [6] | T Weissgaerber.Proc.of Int.Conf.Deformation and Fracture in Struct[A].Materials,Vol.2,IMR SAS,Kosice,1996:163. |
| [7] | Besterici Michal;Ivan Jozef;Kovác Ladislav;Thomas .Sauer,Chista.Strain and fracture mechanism of Cu-TiC[J].Materials Letters,1999,38:270-274. |
| [8] | 赵昆渝,朱心昆,张修庆,林秋实,程抱昌,陈铁力,雍岐龙.自蔓延制备Cu-TiC的研究[J].粉末冶金技术,2001(04):222-224. |
| [9] | 宋桂明,周玉,雷廷权.TiC和ZrC颗粒增强钨基复合材料[J].固体火箭技术,1998(04):54. |
| [10] | Song GM.;Wang YJ.;Zhou Y. .The mechanical and thermophysical properties of ZrC/W composites at elevated temperature[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):223-232. |
| [11] | T. Takida;M. Mabuchi;M. Nakamura;T. Igarashi;Y. Doi;T. Nagae .Mechanical properties of a ZrC-dispersed Mo alloy processed by mechanical alloying and spark plasma sintering[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):269-272. |
| [12] | 李海,刘志义,雷毅,邓小铁.ZrC粒子对低碳钢晶粒细化及力学性能的影响[J].中南工业大学学报(自然科学版),2002(01):71-73. |
| [13] | 高桥辉男;桥本雍彦 .メ力ニ力ルァみロィソグな应用レて制作レたTiCぢょひZrC分散强化铜の开发[J].粉体および粉末冶金(日本),1992,39(07):529. |
| [14] | 张吟秋 等.弥散强化铜微观致密化的研究[J].中南矿冶学院学报,1983,38(04):37-41. |
| [15] | 金属学会;中国有色金属学会.金属材料物理性能手册-第一册:金属物理能及测试方法[M].北京:冶金工业出版社,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%