用偏光显微镜研究了环氧树脂(EP)/液晶化合物固化体系在固化过程中,不同温度、不同反应时间、不同的液晶聚合物加入量下体系的形态变化,用力学方法和差热分析仪(DSC)测试了不同液晶聚合物加入量下固化物的力学性能和玻璃化转变温度(Tg).结果表明:起始固化温度、固化时间、共混方式都对固化体系中液晶的有序结构有较大影响,加入不同含量的液晶聚合物,均可以使固化物的冲击强度、拉伸强度、弯曲强度、模量和Tg提高,其中冲击强度最大提高3.5倍,拉伸强度提高1.6倍,弯曲强度提高1.26倍,弯曲模量提高1.1倍,Tg提高60℃.
参考文献
| [1] | 陈祥宝.高性能树脂基体[M].北京:化学工业出版社,1999 |
| [2] | Barclay G G;Ober C K;Papathomas K I et al.Liquid Crystalline Epoxy Tehermoset Based on Dihydroxymethylstilbene:Synthesis and Characterization[J].Journal of Polymer Science Part A:Polymer Chemistry,1992,30:1821-1843. |
| [3] | Barbaba S;Kurt C F;Piotr P et al.Liquid Crystalline Epoxy Resins by Polyaddition of Aliphatic Dieposides with 4 4'-dihydroxybiphenl[J].Journal of Polymer Science Part A:Polymer Chemistry,1995,33:1275,1281. |
| [4] | Zhang Bao-Long;Tang Guang-Liang;You Ying-Cai;Du Zong-Jie;Huang Ji-Fu .A Study on the Properties of Epoxy Resin Toughened by a Liquid Crystal-Type Oligomer[J].Journal of Applied Polymer Science,1999(1):177-184. |
| [5] | Bao L Z;S W Liao;K Y Shi et al.Modification of Epoxy Resins by Acrylic Copolymers with Side-Chain Mesogenic Units[J].Journal of Applied Polymer Science,1999,73:1787-1792. |
| [6] | 韦春,钟文斌,谭松庭,王霞瑜.热致性液晶固化剂增韧环氧树脂的研究[J].中国塑料,2001(05):42-45. |
| [7] | 韦春,谭松庭,王勇,王霞瑜.热致性液晶聚氨酯的合成研究[J].聚氨酯工业,2001(03):13-16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%