采用高温固相法制备硼酸镁晶须的最佳工艺条件为:焙烧温度大于900℃,焙烧时间为8.0h.制得的晶须粗细均匀,晶型完美,直径约为1.5μm,长度约35μm,长径比约为24.经XRD、SEM和FT-IR分析确定为硼酸镁晶须.以酚醛树脂为基体,添加硼酸镁晶须制备硼酸镁晶须/酚醛树脂复合材料,探讨了硼酸镁晶须添加量和材料厚度对热中子屏蔽率的影响；当硼酸镁晶须添加量为40份时,热中子屏蔽率为73.64％,继续增加添加量,热中子屏蔽率增幅不大；材料厚度为1.0 cm时,热中子屏蔽率为85.01％,继续增加厚度,热中子屏蔽率增加不明显.实验结果表明,以硼酸镁晶须制备聚合物中子屏蔽材料不仅可行,而且对热中子辐射具有较好的屏蔽性能.
参考文献
| [1] | Gencel O;Brostow W;Ozel C et al.An invstigation on the concrete properties containing colemanite[J].Intemational Journal of Physical Sciences,2010,5(03):216-219. |
| [2] | Koichi Okuno .NEUTRON SHIELDING MATERIAL BASED ON COLEMANITE AND EPOXY RESIN[J].Radiation protection dosimetry,2005(1/4):258-261. |
| [3] | 吕继新;陈建廷 .高效能屏蔽材料铅硼聚乙烯[J].核动力工程,1994,15(04):370-374. |
| [4] | Tajiri M;Sunaoka M;Fukumura A et al.Computer modeling of megavoltage X-rays transmission through some shielding materials used in radiotherapy[J].J Mesical Physics,2004,31(11):3022-3023. |
| [5] | G. Arslan;F. Kara;S. Turan .Reaction Model for the Boron Carbide/Aluminium System[J].Key engineering materials,2004(2):1059-1062. |
| [6] | Klein R C;Weilandics C J .Potential health hazards from lead shielding[J].American Industrial Hygiene Association Journal,1996,57(12):1124-1126. |
| [7] | 李清华,岳凌,杨淑琴,陈美玲,朱南康,李欣年,杨占山.中子辐射屏蔽材料PVA/PEO水凝胶的制备及其作用研究[J].辐射研究与辐射工艺学报,2010(02):98-102. |
| [8] | 边绍菊,李洁,乃学瑛,李武.硼酸镁晶须的制备及生长机理初探[J].盐湖研究,2007(02):45-49. |
| [9] | 汪海东,原力,尉敬华,余世英.微波固相法合成硼酸镁晶须[J].盐湖研究,1998(02):98. |
| [10] | 李武,高世扬.纤维硼镁石的高温水热合成研究[J].盐湖研究,1996(03):43. |
| [11] | 樊程芳;吴茂良.核辐射装置及其应用[M].成都:四川大学出版社,1988:58. |
| [12] | 闫长领,卢雁,周建国.MgO·3B2O3-18%MgSO4-H2O过饱和溶液析出固相组成和机理研究[J].物理化学学报,2005(10):1161-1163. |
| [13] | 李哲夫,薛向欣,姜涛.含硼铁精矿粉/环氧树脂复合材料射线屏蔽性能研究[J].功能材料,2010(11):1892-1895. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%