用不锈钢生产中的高碱度二次粉尘制备内配煤团块,在高温下自还原获得含铬、镍的金属铁粒.研究影响铁粒聚集长大的因素.研究表明:(1)内配煤团块的渣相碱度(w( CaO)/w( SiO2))小于2.8时,还原产物冷却过程中渣相与金属铁粒才能自然分离.碱度越低,渣量越大,越不利于金属铁聚集长大；(2)提高内配碳比,渣相残碳量明显升高,渣中过量的碳阻碍金属相聚集长大；(3)提高还原温度,直接还原铁的海绵状结构解体,逐渐聚集成颗粒状金属铁.还原温度越高,越有利于金属铁的聚集长大
参考文献
| [1] | 中国特钢企业协会不锈钢分会对2010年中国不锈钢生产消费情况的统计及分析[OL].http://www.cssc.org.cn/news_ show_content.php? news id =5250,2011-01-27. |
| [2] | Nolasco-Sobrinho P J;Espinosa D C R;Tenorio J A S .Characterization of dusts and sludges generated during stainless steel production in brazilian industries[J].Ironmaking and Steelmaking,2003,30(01):11. |
| [3] | Geldenhuis J M A;Home A W.Recovery of valuables and stabilization of chromium in stainless steel dust fines[A].Nashville,USA,ISS,2002:85:661. |
| [4] | Money K L(Intl.Matals Reclamation CO,Inc);Hanewald.RH;Bleakney R R.Processing steel wastes pyrometallurgically at INMECTCO[A].,2000:397-408. |
| [5] | Verdier,R H (Midrex Corp).Hot briquetted iron. A product for the 1990' S[A].AIME,1991:109-117. |
| [6] | I. Kobayashi;Y. Tanigaki;A. Uragami .A New Process to Produce Iron Directly from Fine Ore and Coal[J].Iron & Steelmaker,2001(9):19-22. |
| [7] | 薛正良,周利刚,张海峰,马国军,吴莉嘉.用含铁物料和煤粉直接制备金属铁粒的新工艺研究[J].武汉科技大学学报(自然科学版),2008(05):453-456. |
| [8] | 张海峰,薛正良,周继程,李小明,陈伟.内配煤团块直接还原法制备铁粒技术研究[J].武汉科技大学学报（自然科学版）,2007(02):125-127,188. |
| [9] | 薛正良,杨叠,周利刚,李莹莹.Wcomet直接还原法渣铁分离影响因素研究[J].武汉科技大学学报（自然科学版）,2009(01):1-4,9. |
| [10] | ZHAO Dong nan;XUE Zheng liang;YANG Die et al.The mechanism of metallic iron aggregation and effect of addition agent on the aggregation of metallic iron during the self-reduction of high basicity coal mixed briquettes[J].Metallurgical International,2011,14(08):10-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%