为研究304不锈钢连铸坯中夹杂物的数量分布,用金相检验法对铸坯中的夹杂物数量进行了统计分析.结果显示,铸坯中由外向内非金属夹杂物数量增加.304不锈钢铸坯表层中绝大多数5 μm以上夹杂物为球状或近似球状的硅酸盐夹杂物.但随着凝固的进行,在铸坯内部会新生大量氧化铝、镁铝尖晶石、氮化物等点状夹杂物和不规则夹杂物.铸坯心部10 μm以上的大颗粒夹杂物数量较多.
参考文献
| [1] | Kim J W;Kim S K;Lee Y D .Formation mechanism of Ca-Si-Al-Mg-Ti-O inclusions in type 304 stainless steel[J].ISIJ International,1996,36(zk):140-143. |
| [2] | Carlo MAPELLI;Paolo NOLLI .Formation Mechanism of Non-Metallic Inclusions in Different Stainless Steel Grades[J].ISIJ International,2003(8):1191-1199. |
| [3] | Todoroki H;Mizuno K .Effect of silica in slag on inclusion compositions in 304 stainless steel, deoxidized with aluminum[J].ISIJ International,2004(8):1350-1357. |
| [4] | 甘志强 .不锈钢夹杂物的成因及降低其含量的途径[J].江西冶金,1998,18(01):9-11. |
| [5] | 郝瑞琴,裴廷振,杨淑菊.18-8型不锈钢夹杂物成因分析及降低其含量途径的研究[J].山西冶金,2000(02):27-28,92. |
| [6] | 范光伟,王贵平,李志斌.0Cr18Ni9不锈钢中非金属夹杂物来源[J].北京科技大学学报,2007(08):776-780. |
| [7] | Mikio SUZUKI;Ryuji YAMAGUCHI;Katsuhiko MURAKAMI .Inclusion Particle Growth during Solidification of Stainless Steel[J].ISIJ International,2001(3):247-256. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%