采用力学性能实验、金相分析以及正交设计实验,研究了单级和多级固溶处理条件对高强Al-Zn-Mg-Cu合金薄板力学性能的影响.结果表明,高强Al-Zn-Mg-Cu合金薄板合适固溶处理温度为470℃,延长固溶处理时间对其横向强度和延伸率不利.250℃×2h+420℃×4h+450℃×3h+470℃×80min的多级固溶处理有提高Al-Zn-Mg-Cu合金薄板强度的作用.470℃最终固溶处理之前的多级预固溶处理有阻碍合金薄板在最终固溶处理时再结晶的作用.
参考文献
| [1] | 林高用,彭大暑,魏圣明,韩红阳,张辉.强化固溶处理对7075铝合金组织的影响[J].金属热处理,2002(11):30-33. |
| [2] | Cantrell .Method of making AA7000 series aluminum wrought product having a modified solution heat treating process for improved exfoliation corrosion resistance[P].U S 5785777,1998. |
| [3] | Kanghua Chen;Hongwei Liu;Zhuo Zhang .The improvement of constituent dissolution and mechanical properties of 7055 aluminum alloy by stepped heat treatments[J].Journal of Materials Processing Technology,2003(1):190-196. |
| [4] | GeorgeRoertSulett .Heat treatment of aluminum[P].US 3305410,1967. |
| [5] | AdrienJ;Maire E;Estevez R et al.InfluenceofthethermomechanicaltreatmentonthemicroplasticbehaviorofawroughtAl-Zn-Mg-Cualloy[J].Acta Materialia,2004,52(06):1653-1661. |
| [6] | LinJ;Kersker M M .Heat treatment of precipitation hardening alloys[P].U S: 5108520,19924. |
| [7] | 苏学常;徐佩玉.7075合金的组织过烧[J].轻金属,1985(03):45-48. |
| [8] | 唐伟;张华;马英义 .7475-T7351厚板热处理工艺研究[J].轻合金加工技术,1999,27(08):20-24. |
| [9] | 宋仁国.形变、固溶和时效制度对7175铝合金强度的影响[J].有色矿冶,1994(06):29-32. |
| [10] | 影响铝合金固溶保温时间的多因素相关规律[J].中国有色金属学报,1999(01):79. |
| [11] | 张华;王学书;海朝智 .7075-T651板材生产工艺的研究[J].轻合金加工技术,1997,25(07):28-30. |
| [12] | 宁爱林,曾苏民,莫亚武,罗玉梅.超高强铝合金的回顾与展望[J].邵阳学院学报,2003(05):90-92. |
| [13] | 陈康华,黄兰萍.Effect of high-temperature pre-precipitation on microstructure and properties of 7055 aluminum alloy[J].中国有色金属学会会刊(英文版),2003(04):750-754. |
| [14] | M. Iskandar;D. Reyes;Y. Gaxiola .On identifying the most critical step in the sequence of heat treating operations in a 7249 aluminum alloy[J].Engineering failure analysis,2003(2):199-207. |
| [15] | 中国科学院数学研究所统计组.常用数理统计方法[M].北京:科学出版社,1974:34-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%