利用热模拟压缩试验测定了不同钒含量的钒微合金化低碳钢在900～1000℃温度区间和0.1～1s-1变形速率范围内的真应力-真应变曲线.对曲线的分析表明:随钢中钒含量的增加,低碳钢的动态再结晶开始时间延长,变形奥氏体的动态再结晶名义激活能提高.实验钢薄膜试样的TEM观察表明,钢中的微量钒以固溶态存在于奥氏体中,微量的固溶钒对奥氏体动态再结晶起到抑制作用.
参考文献
| [1] | WeissI;Jonas J J .InteractionbetweenrecrystallizationandprecipitationduringthehightemperaturedeformationofHSLAsteels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1979,10:831-840. |
| [2] | LutonMJ;Dorvel R;Petkovic R A .Interactionbetweendeformation,recrystallizationandprecipitationinniobiumsteels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1980,11:411-420. |
| [3] | 程晓茹;李虎兴;郑琳 等.管线钢X65高温变形再结晶研究[J].金属学报,1997,33(12):1275-1281. |
| [4] | JonasJJ;Weiss I .Effectofprecipitationonrecrystallizationinmicroalloyedsteels[J].Metal Science Journal,1979,13:238-245. |
| [5] | 斯坦尼什洛·扎雅克 .含钒钢的沉淀和晶粒细化[J].钢铁钒钛,2002,23(01):35-48. |
| [6] | AkenMG;Bacroix B;Jonas J J .Effectofvanadiumandmolybdenumadditiononhightemperaturerecovery,recrystallizationandprecipitationbehaviorofniobium-basedmicroalloyedsteels[J].Acta Materialia,1983,31(01):61-174. |
| [7] | 王凯 .热变形参数对X60管线钢高温变形行为和组织性能的影响[D].东北大学,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%