研究了固体体积分数和琼脂质量分数对SiC浆料表观粘度的影响规律,并在确定琼脂质量分数为0.5%的条件下,研究了碳化硅体积分数对浆料原位凝固成型后坯体的体积密度和收缩率的影响规律.研究结果表明,SiC陶瓷浆料表观粘度随着碳化硅体积分数和琼脂质量分数的增加而增加,而原位凝固成型后坯体的收缩率则随之降低;当浆料中碳化硅的固相体积分数为55%、琼脂质量分数为0.5%时,浆料具有良好的流动性,其表观粘度小于1Pa*s;利用琼脂原位凝固注模成型后坯体收缩率为0.6%、体积密度为2.18g*cm-3,坯体表面光滑、内部无大气孔、并且具有非常好的脱模强度,完全能满足工业生产的要求.
参考文献
| [1] | GaulcklerLJ;Graule T J;Baader F H .Ceramicformingusingenzymecatalyzedreaction[J].Materials Chemistry and Physics,1999,61(01):78-102. |
| [2] | YOUNGAC;Omatete O O;Janney M A.Gelcastingofalumina[J].Journal of the American Ceramic Society,1991(74):612-618. |
| [3] | OmateteOO;Janney M A;Nunn S D .Gelcasting:FromLaboratoryDevelopmentTowardIndustrialProduction[J].Journal of the European Ceramic Society,1997,17(2-3):407-413. |
| [4] | GilissenR;Erauw J P;Smolders A .Gelcastinganearnetshapetechnique[J].Materials & Design,2000,21(04):251-257. |
| [5] | OmateOO;Janney M A;Strehlow R A .Gelcastinganewceramicformingprocess[J].American Ceramic Society Bulletin,1991,70(10):1641-1649. |
| [6] | Janney MA.;Walls CA.;Nunn SD.;Ogle RJ.;Westmoreland G.;Omatete OO. .Development of low-toxicity gelcasting systems[J].Journal of the American Ceramic Society,1998(3):581-591. |
| [7] | WangX;Xie Z P;Huang Y et al.Gelcastingofsiliconcarbidebasedongelationofsodiumalginate[J].Ceramics International,2002,28(08):865-871. |
| [8] | 谢志鹏,杨金龙,陈亚丽,黄勇.琼脂糖凝胶大分子在陶瓷原位凝固成型中的应用[J].硅酸盐学报,1999(01):16-21. |
| [9] | Y.Chen and Y.Huang .Alumina casting based on gelation of gelatine[J].Journal of the European Ceramic Society,1999(2):271-275. |
| [10] | 谭佩幸;陶宗晋;祁国荣.现代化学试剂手册第三分册生化试剂(二)[M].北京:化学工业出版社,1991:146-149. |
| [11] | 沈钟;王果庭.胶体与表面化学[M].北京:化学工业出版社,1997:104-144. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%