用阿基米德实验方法,采用二次正交回归实验设计,研究了低温铝电解质Na3AlF6-AlF3-Al2O3-CaF2-MgF2-NaCl体系的密度.得到密度(ρ)与温度(t/℃)、分子比(CR)和NaCl质量分数(B/%)关系的简化方程:ρ=2.7305-1.225×10-3t+2.204×10-1 (CR)-2.014×10-3 (B-8.292)2.绘制了低温铝电解质密度的等值面图,并讨论了各因素对低温铝电解质密度的影响.经计算得出了实验条件下的密度为1.80～2.05 g/cm3,并与该电解工艺条件下的铝液密度对比,讨论了铝液与低温铝电解质的分离效果.
参考文献
| [1] | 卢惠民;邱竹贤 .低温铝电解的研究进展[J].轻金属,1997,22(04):24-28. |
| [2] | 卢惠民,邱竹贤,方克明,洪彦若.在Na3AlF6-AlF3-CaF2-LiF-Al2O3体系中低温铝电解[J].北京科技大学学报,1999(04):324-326. |
| [3] | 邱竹贤.铝电解原理与应用[M].徐州:中国矿业大学出版社,1998:84-92. |
| [4] | Grjotheim K;Kvande H;Welch B J .Low-melting baths in aluminium electrolysis[J].Metallurgical Soc of AIME,1986,2:417-423. |
| [5] | Chrenkova M;Danek V;Silny A.Density,electrical conductivity and viscosity of low melting baths for aluminium electrolysis[J].Light Metals:proceedings of sessions,TMS annual meeting(Warrendale,Pennsylvania),1996:227-232. |
| [6] | Sleppy W C;Cochran C N .Bench scale electrolysis of alumina in sodium fluoride-aluminium fluoride melts below 900 degree C[J].Aluminium,1979,55(09):604-606. |
| [7] | Lu Huimin,Qiu Zhuxian,Fang Keming.LOW TEMPERATURE ALUMINUM ELECTROLYSIS IN NaF-AlF3-BaF2-CaF2 BATH SYSTEM[J].中国有色金属学会会刊（英文版）,1999(02):383-386. |
| [8] | Lu H M;Fang K M;Qiu Z X .Low temperature aluminum floating electrolysis in heavy electrolyte Na3AlF6-AlF3-BaCl2-NaCl bath system[J].Acta Metallurgica Sinica(English Lett),2000,13(04):949-954. |
| [9] | Qiu Z X;Li Q F;Ho M H.Aluminum electrolysis at low temperature[J].Light Metals:Proceedings of Sessions,AIME Annual Meeting(Warrendale,Pennsylvania),1985:529-544. |
| [10] | Grjotheim K;Thonstad J;Matiasovsky K .Energy efficiency and bath composition in aluminium electrolysis[J].Aluminium,1973,49(12):803-807. |
| [11] | 佐藤让;小岛彰;江岛辰彦 .密度の测定[J].日本金属学会志(日本),1977,56(12):1249-1253. |
| [12] | 付静 .低温铝电解质密度及熔盐电解法制取铝铒合金的研究[D].东北大学,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%