通过浸渍干湿循环加速腐蚀试验,采用失重法测量年蚀率,SEM观察腐蚀产物的表面形貌和断面形貌,XRD测定腐蚀产物的物相组成,电化学阻抗谱仪测定锈层的交流阻抗谱,研究了09CuPTiRE耐候钢与Q235、鞍钢耐候钢和日本耐候钢三种参比钢的耐候性能及腐蚀过程.结果表明:09CuPTiRE钢的耐候性能显著优于Q235钢;Q235钢锈层为一层网状、疏松且有大量纵向交错裂纹和孔洞的锈层,而09CuPTiRE及另两种耐候钢的锈层分内外两层,外层与Q235钢锈层相似,内层均匀、连续、致密;Q235钢的腐蚀过程受活化控制,即受控于金属离子进入溶液的速度,而09CuPTiRE钢的腐蚀过程既受活化控制,由于保护锈层的存在还受氧的扩散控制.
参考文献
| [1] | 王祖滨;东涛.低合金高强度钢[M].北京:原子能出版社,1996:196-214. |
| [2] | 傅作宝;曹荫之.钢铁研究成果荟萃[M].沈阳:辽宁科学技术出版社,1993:2-5,43-44. |
| [3] | Yamashita M;MIYUKI Y .The long term growth of the protective rust layer formed on weathering steel by atmospheric corrosion during a quarter of a century[J].Corrosion Science,1994,36(02):283-289. |
| [4] | 陈亮;刘正生;吴立新 等.耐大气腐蚀钢锈层的X射线衍射与SEM分析[J].钢铁研究,1994,76(01):32-36. |
| [5] | Cook D C;VAN ORDEN A C;CARPIO J J;OH S J .Atmospheric corrosion in the Gulf of Mexico[J].Hyperfine Interactions,1998,113:319-329. |
| [6] | Nishikata A;ICHIHARA Y;SURU T T .An application of electrochemical Impedance spectroscopy to atmospheric corrosion study[J].Corrosion Science,1995,6:897-911. |
| [7] | 张万灵;刘建容 .交流阻抗法对耐候钢腐蚀行为的研究[J].钢铁研究,1996,92(05):39-43. |
| [8] | 田妮 .09CuPTiRE钢耐候性能及耐候机理研究[D].东北大学,2003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%