以对苯二甲酸和癸二胺为原料,经成盐、预聚合和固相聚合三个步骤合成了新型长碳链和较高分子量的半芳香尼龙聚对苯二甲酰十碳二胺(PA10T).用TG-DTG方法研究了PA10T的热降解和热降解动力学,结果表明,PA10T的热分解为一步降解,其起始平衡降解温度为435.3 ℃,终止平衡降解温度为470.7 ℃,最大降解速率时平衡降解温度为459.5 ℃.通过微分法和积分法计算出PA10T的热分解活化能分别为274.4 kJ mol-1和263.96～290.37 kJ mol-1之间,其耐热性能优于脂肪族尼龙.
参考文献
| [1] | Wang XC;Zheng Q;Du LB;Yang GS .Influence of preparation methods on the structures and properties for the blends between polyamide 6co6T and polyamide 6: Melt-mixing and in-situ blending[J].Journal of Polymer Science, Part B. Polymer Physics,2008(2):201-211. |
| [2] | Endo M;Morishima Y;Yano S;Tadano K;Murata Y;Tsunashima K .Miscibility in binary blends of aromatic and alicyclic polyamides[J].Journal of Applied Polymer Science,2006(6):3971-3978. |
| [3] | Uddin AJ.;Ohkoshi Y.;Gotoh Y.;Nagura M.;Hara T. .Influence of moisture on the viscoelastic relaxations in long aliphatic chain contained sem-iaromatic polyamide, (PA9-T) fiber[J].Journal of Polymer Science, Part B. Polymer Physics,2003(22):2878-2891. |
| [4] | 张红荣,魏运方.高性能半芳香族尼龙工程塑料的性能及应用进展[J].精细化工中间体,2002(06):1-4. |
| [5] | 吕世光.聚合物的稳定化[M].北京:中国轻工业出版社,1986:182. |
| [6] | 张成贵,刘民英,赵清香,王玉东,曹少魁.尼龙1212的热降解过程和机理研究[J].塑料工业,2002(06):38-40,53. |
| [7] | 王志敏,王玉东,赵清香,刘民英,申小清,张勇,赵天增.石油发酵尼龙1313热降解性能的研究[J].工程塑料应用,2003(08):7-10. |
| [8] | 席国喜,宋世理,刘琴.金属氧化物催化热降解废聚甲基丙烯酸甲酯的动力学研究[J].石油化工,2005(03):250-253. |
| [9] | 王亚明,刘岚,罗远芳,贾德民.氟橡胶/改性乙丙橡胶并用胶的热稳定性[J].物理化学学报,2008(06):1100-1104. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%