对均匀温度场中制得的聚氨酯脲弹性体在梯度温度场中进行梯度热处理,控制不同的温度梯度和处理时间,得到一系列试样.用傅立叶变换红外光谱(FTIR)对试样进行表征,结果表明,梯度热处理试样的结构呈现梯度变化的趋势.在试样内部从高温到低温端微相分离程度逐渐降低.并且热处理的温度梯度越大或时间越长,相分离的梯度也越大.拉伸测试表明,热处理提高了试样的拉伸强度,断裂伸长率却有所下降.
参考文献
| [1] | Mutsuhisa Furukawa;Yoshitaka Mitsui;Tomoya Fukumaru;Ken Kojio .Microphase-separated structure and mechanical properties of novel polyurethane elastomers prepared with ether based diisocyanate[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(24):10817-10822. |
| [2] | Velankar S.;Cooper SL. .Microphase separation and rheological properties of polyurethane melts. 1. Effect of block length[J].Macromolecules,1998(26):9181-9192. |
| [3] | Velankar Sachin;Cooper< Stuart L. .Microphase Separation and Rheological Properties of Polyurethane Melts. 3. Effect of Block Incompatibility on the Viscoelastic Properties[J].Macromolecules,2000(2):395-403. |
| [4] | 罗宁;王得宁;应圣康.变温红外光谱研究多嵌段聚氨酯脲的微相分离行为[J].高分子学报,1996(04):423-428. |
| [5] | 李再峰,张田林,徐春明.FTIR研究热处理对RIM PUU的形态及力学性能的影响[J].光谱学与光谱分析,2004(09):1066-1068. |
| [6] | 俞炜,周持兴.温度梯度引起的聚合物共混物梯度相形态的研究[J].高等学校化学学报,2001(02):321-324. |
| [7] | 张超灿,黄芳,韦丽莉,吴力立.梯度功能高分子材料的研究[J].武汉理工大学学报,2002(10):13-16. |
| [8] | 赵培仲,花兴艳,朱金华,王源升.利用粘弹性阻尼结构研究聚氨酯的阻尼性能[J].弹性体,2005(02):37-39. |
| [9] | Li W.;Ryan AJ.;Meier IK. .Morphology development via reaction-induced phase separation in flexible polyurethane foam[J].Macromolecules,2002(13):5034-5042. |
| [10] | 罗宁;王得宁;应圣康 .聚氨酯红外光谱氢键化谱带的归属与定量分析[J].合成橡胶工业,1995,18(04):200-203. |
| [11] | Paik Sung C S;Smith T W;Sung N H .Properties of segmented polyether poly(urethaneureas) based on 2,4-toluene diisocyanate.2.infrared and mechanical studies[J].Macromolecules,1980,13(01):117-121. |
| [12] | 赵孝彬,杜磊,张小平,郑剑.聚氨酯弹性体及其微相分离[J].高分子材料科学与工程,2002(02):16-20. |
| [13] | 陈建钧,涂善东,王正东.梯度涂层界面裂纹蠕变扩展驱动力的研究[J].机械强度,2005(02):227-231. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%