对50钢进行了正火+高温回火、中温回火、高温回火三种不同热处理状态的对称拉压超声疲劳试验,同时用扫描电子显微分析技术和X射线能谱分析方法对50钢的疲劳断口形貌进行显微分析,研究其疲劳断裂行为和疲劳断裂机理.结果表明,50钢存在表面和内部两种裂纹萌生机制;在本试验范围内,热处理工艺对50钢超高周疲劳性能的影响较低周和高周为小,随着寿命的增加,影响越来越弱;热处理工艺对50钢不同的疲劳阶段有不同的影响起源于不同的裂纹萌生机制,对常规疲劳性能起改善作用的热处理工艺可能对材料超高周疲劳性能的改善没有太大作用.
参考文献
| [1] | Shiozawa K;LU L;Ishihara S .S-N curve characteristics and subsurface crack initiation behavior in ultra-long life fatigue of a high carbon-chromium bearing steel[J].Fatigue and fracture of engineering materials and structures,2001,24:781-790. |
| [2] | LU L;Shiozawa K;Ishihara S .Characteristic of S-N curve and subsurface crack initiation behavior of high strength bearing steel in gigacycle fatigue[J].Mat Sic Res Int,2001,STP-1:35-40. |
| [3] | Shiozawa K;LU L .Very high-cycle fatigue behavior of shot-peened high-carbon-chromium bearing steel[J].Fatigue Fract Engng Mater Struc,2002,28(8-9):813-822. |
| [4] | Bathias C;Drouillac L;Francois P Le .How and why the fatigue S-N ctrve does not approach ahorizontal asymptote[J].International Journal of Fatigue,2001,23:S143-S151. |
| [5] | 王弘,高庆.超声疲劳扭转试样谐振长度的解析法计算[J].西南交通大学学报,2001(06):595-598. |
| [6] | 闫桂玲,王弘,高庆.超声疲劳试验方法及其应用[J].力学与实践,2004(06):25-29. |
| [7] | 闫桂玲,王弘,高庆.超声频率加载下50#车轴钢超长寿命疲劳性能研究[J].中国铁道科学,2004(02):78-81. |
| [8] | 王弘 .40Cr、50车轴钢超高周疲劳性能研究及疲劳断裂机理探讨[D].西南交通大学,2004. |
| [9] | 束德林.工程材料力学性能[M].北京:机械工业出版社,2003:112-138. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%