采用低温化学镀方法在超细WC颗粒表面进行金属钴包覆,烧结包覆后的复合粉体制备新型硬质合金NYG(WC-3%Co).研究了超细WC-Co硬质合金的力学性能、断口形貌和显微结构,在销盘式磨损试验机上进行干滑动磨损实验.结果表明,在硬质合金烧结过程中,沿WC晶界均匀分布的金属钴不仅起粘结剂作用,也起抑制剂作用阻碍晶粒的长大;新型硬质合金的抗弯强度、断裂韧性、硬度和耐磨性能均得到较大提高;在干滑动摩擦条件下,新型WC-Co硬质合金的失效以塑性变形及细小碳化钨相颗粒脱落为特征.
参考文献
| [1] | Carroll D F.Processing and properties of ultrafine WC/Co hard materials[A].China,1998:79-86. |
| [2] | 陆远明 .WC-Co硬质合金的断裂韧性与其成分和结构的关系[J].硬质合金,1988,5(03):1-5. |
| [3] | Medeiros FFP.;De Souza CP.;Da Silva AGP.;Gomes UU.;De Souza JF.;De Oliveira SA. .Synthesis of tungsten carbide through gas-solid reaction at low temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):58-62. |
| [4] | 高荣根.纳米结构WC-Co复合粉末的制备与应用[J].稀有金属与硬质合金,1996(137):49. |
| [5] | Joanna R. Groza .Sintering of nanocrystalline powders[J].International Journal of Powder Metallurgy,1999(7):59-66. |
| [6] | Rajendra K. Sadangi;Larry E. McCandlish;Bernard H. Kear;Purnesh Seegopaul .Grain growth inhibition in liquid phase sintered nanophase WC/Co alloys[J].International Journal of Powder Metallurgy,1999(1):27-33. |
| [7] | 王兴庆,郭海亮,何宝山.纳米硬质合金制备技术的研究[J].硬质合金,2003(01):1-6. |
| [8] | 赵海锋,朱丽慧,马学鸣.纳米WC硬质合金制备新工艺[J].材料科学与工程学报,2003(01):130-133. |
| [9] | 姜晓霞;沈维.化学镀理论及实践[M].北京:国防工业出版社,2000 |
| [10] | Huang L P;Li J .Properties of cobalt-reinforced Al2O3-TiC ceramic matrix composite made via a new processing route[J].Composites Part A:Applied Science and Manufacturing,1999,30(03):615-618. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%