研究了近门槛区单周过载对40Cr钢热处理组织Ⅰ型疲劳门槛的影响.实验表明:四种组织过载后疲劳门槛均会提高,其幅度随过载比的加大和材料屈服强度的降低而增加;过载效应是裂尖钝化、裂尖附近残余压应力和裂尖尾部塑性诱导闭合等共同作用的结果.控轧控冷组织与正火组织、锻热淬火组织与调质组织分别对比,各自具有相近的疲劳裂纹过载效应.
参考文献
| [1] | 李春雨,粱浩华.40Cr钢连杆锻热淬火工艺及其应用[J].新技术新工艺,1996(02):25-26. |
| [2] | 胡静,丁国裕.YF40MnV易切削非调钢楔横轧工艺试验与应用[J].机械工程材料,2001(04):27-28,38. |
| [3] | 李智;乔兵;王国栋.汽车用非调质钢及其控轧控冷工艺[J].汽车工艺与材料,1999(03):10-13. |
| [4] | 王章忠 .Ⅰ、Ⅱ、Ⅲ型过载对Ⅰ型疲劳裂纹近门槛区扩展特性的影响[D].西安交通大学,1990. |
| [5] | Topper T H;Yu M T .The effect of orerloads on threshold and crack closure[J].International Journal of Fatigue,1985,7(03):159-164. |
| [6] | Oktem V .Effect of single overload in F C P[J].Engineering Fracture Mechanics,1988,30(03):329-335. |
| [7] | Elber W .The significance of fatigue crack closure[Z].ASTM STP486,1971. |
| [8] | Shin O S;Fleck N A .Overload retardation in a structural steel[J].Fatigue & Fracture of Engineering Material & Structure,1987,9(09):379-393. |
| [9] | Williams J F;Stouffer D C .An estimate of the residual stress distribution in the vicinity of a propagation fatigue crack[J].Engineering Fracture Mechanics,1979,11(03):547-557. |
| [10] | Beevers C J;Bell K;Carlson R L .A model for fatigue crack closure[J].Engineering Fracture Mechanics,1984,19:93-100. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%