以双酚芴、十氟联苯和磺化二氟酮为单体,合成磺化含氟聚芴醚酮(Sulfonated-fluo-rinated nuorene-containing poly(arylene ether ketone)s,SFPEEK).SFPEEK可溶于极性有机溶剂,具有较高的黏度,易于浇铸形成柔韧透明的薄膜.用其制成的质子交换膜表现出良好的热稳定性和抗水解、抗氧化性能.在相同测试条件下,SFPEEK膜具有与杜邦公司Nation 117膜相当的质子电导率,同时,具有比Nafion 117更好的耐甲醇渗透性能.直接甲醇燃料电池(DMFC)单池测试表明,放电到0.2 V时,用SFPEEK膜制备的单池电流密度可达66 mA/cm~2,电池性能优于相同条件下用Nafion117膜组装的单池(电流密度60 mA/cm~2).
Sulfonated- fluorinated fluorene- containing poly(arylene ether ketone)s (SFPEEK) were synthe-sized from 9,9-bis(4-hydroxyphenyl) fluorene, decafluorobiphenyl and sulfonated 4,4'-diflourobenzophenone (SDFBP).The resulting sulfonated poly(arylene ether ketone)s are soluble in polar organic solvents with high inherent viscosity (3.95 dL/g) and can form flexible and transparent membranes by casting from their solution.The membrane showed high thermal, hydrolysis stability and superior anti- oxidative stability.The proton con-ductivity of the membrane was determined to be equivalent with Nation 117 under the identical conditions.The methanol penetrability of the prepared membrane was 4.4 × 10~(-7) cm~2/s,while that of Nation 117 was 1.32× 10~(-6) cm~2/s under the identical conditions.The DMFC single cell was assembled using the as- prepared mem-branes for evaluation, and the current densities were 66 and 60 mA/cm~2 at the potential of 0.2 V for the SFPEEK membrane and Nation 117 membrane respectively.So the novel polymer was demonstrated its poten-tial application as a proton exchange membrane for direct methanol fuel cell (DMFC).
参考文献
| [1] | Shoesmith J P;Collins R D;Oakhy M J et al.Status of solid polymer fuel cell system development[J].Journal of Power Sources,1994,49:129-142. |
| [2] | Bishop M T;Karasz F E;Russo P S et al.Solubility and properties of a poly(aryl ether ketone) in strong acids[J].Macromolecules,1985,18:86-93. |
| [3] | Miyatake K;Shoyji E;Yamamoto K et al.Synthesis and proton conductivity of highly sulfonated poly (tbio2 phenylene)[J].Macromolecules,1997,30:2 941. |
| [4] | Wang F.;Ji Q.;Harrison W.;Mecham J.;Zawodzinski TA. McGrath JE.;Hickner M. .Synthesis of highly sulfonated poly(arylene ether sulfone) random (statistical) copolymers via direct polymerization[J].Macromolecular symposia,2001(0):387-395. |
| [5] | Basura V I;Beattie P D;Holdcroft S .Solid-state dectrochemical oxygen reduction at Pt/Nafion 117 and Pt/BAM3G (tm) 407 interfaces[J].Journal of Electroanalytical Chemistry,1998,458:1-5. |
| [6] | Agostino D;Lee J Y Jr;Cook E H .[P].US Pat 4012303,1977-3-15. |
| [7] | Paul D. Beattie;Vesna I. Basura;Steven Holdcroft .Temperature and pressure dependence of O_2 reduction at Pt|Nafion 117 and Pt|BAM 407 interfaces[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,1999(2):180-192. |
| [8] | Miyataka K;Oyaizu K;Tsuchida E;Hay A S .Synthesis and properties of novel sulfonated arytene ether/fluorinated alkane copolymers[J].Macromolecules,2001,34:2 065-2 071. |
| [9] | Miyatake K;Hay A S .Synthesis and properties of poly (arylene ether)s beating sulfonic acid groups on pendant phenyl tings[J].Journal of POLYMER SCIENCE PART A:POLYMER CHEMISTRY,2001,39:3 211-3 217. |
| [10] | Chen YL;Meng YZ;Wang SJ;Tian SH;Chen Y;Hay AS .Sulfonated poly(fluorenyl ether ketone) membrane prepared via direct polymerization for PEM fuel cell application[J].Journal of Membrane Science,2006(1/2):433-441. |
| [11] | 田双红,舒东,孟跃中.一种含芴聚芳醚酮质子交换膜的合成与表征[J].膜科学与技术,2008(02):18-21. |
| [12] | Wang F.;Xu JP.;Chen TL. .Sodium sulfonate-functionalized poly(ether ether ketone)s[J].Macromolecular chemistry and physics,1998(7):1421-1426. |
| [13] | Shang XY;Shu D;Wang SJ;Xiao M;Meng YZ .Fluorene-containing sulfonated poly(arylene ether 1,3,4-oxadiazole) as proton-exchange membrane for PEM fuel cell application[J].Journal of Membrane Science,2007(1/2):140-147. |
| [14] | Dai H;Guan R;Li C H et al.Eevelopment and characterization of sulfonated poly(ether sulfone) for proton exchange membrane materials[J].Solid State Ionics,2007,178:339-345. |
| [15] | Lufrano F;Squadrito G;Patti A;Passalacqua E .Sulfonated polysulfone as promising membranes for polymer dectrolyte fuel cells[J].Journal of Applied Polymer Science,2000,77:1 250-1 256. |
| [16] | K.D. Krueuer .On the development of proton conducting polymer membranes for hydrogen and methanol fuel cells[J].Journal of Membrane Science,2001(1):29-39. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%