采用动态水热法在α-Al2O3陶瓷管载体内表面合成出致密的NaA分子筛膜.利用SEM、XRD和单组分气体渗透等方法对NaA分子筛膜表征.由XRD确定合成出的为NaA分子筛膜;由SEM照片观察到分子筛膜表面平整,分子筛晶粒均匀,膜厚约为20μm;通过单组分气体渗率测得H2/N2和H2/C3H8的理想分离因数分别为3.38和4.87,达到了Knudsen扩散机制的水平.
参考文献
[1] | 董强,徐南平,时钧.A型沸石分子筛膜微波合成及渗透汽化性能[J].化工学报,2001(08):749-752. |
[2] | 董强,徐南平,时钧.铝硅酸溶液中NaA型沸石分子筛膜合成规律的研究[J].硅酸盐通报,2002(01):54-57. |
[3] | 梁玉秀,鲁金明,李邦民,王金渠,殷德宏.在粗孔αAl2O3载体上合成NaA沸石膜[J].过程工程学报,2003(03):251-255. |
[4] | Xiaochun Xu;Weishen Yang;Jie Liu;Liwu Lin .Synthesis of NaA zeolite membranes from clear solution[J].Microporous and Mesoporous Materials,2001(3):299-311. |
[5] | 方永浩,杨南如,钱同生.有支撑纯NaA和NaY沸石膜的合成[J].硅酸盐通报,1999(02):29-31. |
[6] | Boudreau Laura C.;Tsapatsis Michael;Kuck Julia A. .Deposition of oriented zeolite A films: In situ and secondary growth[J].Journal of Membrane Science,1999(1):41-59. |
[7] | Satoshi Y;Kazuo T .Synthesis of A-type zeolite membrane using a plate heater and its bormation mechanism[J].Microporous and Mesoporous Materials,2000,37:67-80. |
[8] | 申少华,李爱玲,张术根,王大伟.A型沸石的水热制备及生长机制研究[J].硅酸盐学报,2003(08):732-737. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%