利用熔融法制备了一系列具有不同纳米碳管含量的纳米碳管(CNT)/高密度聚乙烯(HDPE)复合材料.对其拉伸性能的研究结果表明,添加质量分数分别为2 %,5 %和10 %的纳米碳管使HDPE的拉伸模量分别提高了7.4 %,27.0 %和28.6 %,屈服强度分别提高了3.3 %,14.4 %和18.5 %,但是会降低HDPE的断裂强度和断裂伸长率.同时,对复合材料中HDPE结晶过程的研究表明,纳米碳管可以提高HDPE的开始结晶温度,降低结晶活化能,但是会使HDPE的结晶速率下降,结晶度降低.
参考文献
| [1] | Calvert P .A recipe for strength[J].Nature,1999,399:210-211. |
| [2] | Qian D;Wagner G J;Liu W K et al.Mechanics of carbon nanotubes[J].Applied Mechanics Reviews,2003,15(06):495-533. |
| [3] | Erik T. Thostenson;Zhifeng Ren;Tsu-Wei Chou .Advances in the science and technology of carbon nanotubes and their composites: a review[J].Composites science and technology,2001(13):1899-1912. |
| [4] | 李莉香,李峰,英哲,杨全红,成会明.纳米碳管/聚合物功能复合材料[J].新型炭材料,2003(01):69-74. |
| [5] | 李玉宝,解思深,周维亚,王刚,魏秉庆,吴德海.碳纳米管对Fe-P非晶的力学性能和晶化行为影响的研究[J].新型炭材料,2000(03):7-12. |
| [6] | 张滨,刘畅,成会明,才庆魁.纳米碳管内包覆外来物质的研究进展[J].新型炭材料,2003(03):174-180. |
| [7] | 陈晓红,宋怀河.多壁碳纳米管填充丁苯橡胶复合材料的研究[J].新型炭材料,2004(03):214-218. |
| [8] | 杨凤,赵海超,张学全,黄葆同,冯之榴.原位聚合制备聚乙烯/蒙脱土（MMT）纳米复合材料的研究[J].高等学校化学学报,2003(04):711-714. |
| [9] | Wenzhong Tang;Michael H.Santare;Suresh G.Advani .Melt processing and mechanical property characterization of multi-walled carbon nanotube/high density polyethylene (MWNT/HDPE) composite films[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(14):2779-2785. |
| [10] | Dufresne A.;Paillet M.;Putaux JL.;Canet R.;Carmona F.;Delhaes P.;Cui S. .Processing and characterization of carbon nanotube/poly(styrene-co-butyl acrylate) nanocomposites[J].Journal of Materials Science,2002(18):3915-3923. |
| [11] | 刘晓辉,范家起,漆宗能.聚丙烯/蒙脱土纳米复合材料的非等温结晶动力学研究[J].高分子材料科学与工程,2001(06):103-105,110. |
| [12] | Liu TX;Mo ZS;Wang SG;Zhang HF .Nonisothermal melt and cold crystallization kinetics of poly(aryl ether ether ketone ketone)[J].Polymer engineering and science,1997(3):568-575. |
| [13] | 徐卫兵,戈明亮,何平笙.聚丙烯/蒙脱土纳米复合材料非等温结晶动力学的研究[J].高分子学报,2001(05):584-588. |
| [14] | 曾继军,李育英,何嘉松,陈伟.茂金属聚乙烯的非等温结晶动力学[J].高分子学报,1999(03):280-286. |
| [15] | Xu WB.;Liang GD.;Zhai HB.;Tang SP.;Hang GP.;Pan WP. .Preparation and crystallization behaviour of PP/PP-g-MAH/Org-MMT nanocomposite[J].European Polymer Journal,2003(7):1467-1474. |
| [16] | 刘振海.分析化学手册[M].北京:化学工业出版社,2000:47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%