采用三种不同型号的防锈油对HDDR-NdFeB磁粉进行表面处理,将处理后的磁粉用压延工艺制备成柔性片状磁体.研究了处理后的磁粉制备的磁体的抗氧化性能、力学性能和磁性能.结果表明表面处理后的磁粉制备的磁体的抗氧化性能和磁性能均有所提高.防锈油处理能大幅度提高磁体的韧性和柔性,断裂拉伸率最高可达389%,但会降低磁体强度.防锈油处理磁粉后,磁体的添粉量可以大幅提高,对于100目的磁粉,磁粉与橡胶比值由10提高到25,最大磁能积提高了41.2%.
The HDDR-NdFeB powders are coated with three kinds of anticorrosion oil.The oxidation behaviors,mechanical and magnetic properties of the flexible bonded magnets produced by the treated powders using calendering technics are systematically studied.The experimental results shows that all the treatments can improve the anticorrosion properties of the magnets.The treatment of anticorrosion oil can enhances the resilience and flexible of magnets,whose maximal elongation is as high as 389%,but can reduces the tensile strength of the magnets simultaneously.In the process of calendaring,anticorrosion oil can enhance the anticorrosion property of magnetic powders.The ratio of magnetic powders(standard sieve of 100-mesh)to rubber can be substantially increased from 10:1 to 25:1 on account of anticorrosion oil,and the(BH)max can be enhanced by41.2%.
参考文献
| [1] | 王峰,陶振声,李亚峰,黄可淼,任先京.柔性橡胶钕铁硼粘结磁体增塑-补强体系的优化设计[J].磁性材料及器件,2005(03):39-42. |
| [2] | 王峰,任先京,陶振声.偶联剂和固化剂对柔性橡胶钕铁硼复合材料性能的影响[J].磁性材料及器件,2003(06):10-12,18. |
| [3] | GB/T 528-1998.GB/T 528-1998.硫化橡胶或热塑性橡胶-拉伸应力应变性能的测定[S]. |
| [4] | 刘亚东.充油稀土顺丁橡胶的加工工艺性质[A].北京:科学出版社,1980:297. |
| [5] | 王立军,刘军.填充油对充油丁苯橡胶性能的影响[J].齐鲁石油化工,2008(03):182-185. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%