采用放电等离子烧结技术(spark plasma sintering,简称SPS)制备了高性能新型NdFeB永磁材料.研究了热处理工艺对SPS NdFeB磁体的组织和性能影响,采用扫描电镜、B-H回线仪研究磁体的显微组织和磁性能.结果表明,不同烧结温度的SPS烧结体对不同温度的热处理表现出同样的规律性,最佳热处理温度为1050℃.SPS NdFeB磁体的热处理过程,富稀土相成分和结构发生改变.在优化工艺条件下制备出最佳性能为Br=1.351T,Hci=674.4kA·m-1,BHm=360.4 kJ·m-3的新型SPS NdFeB磁体.
参考文献
[1] | Takeshita T.;Morimoto K. .ANISOTROPIC ND-FE-B BONDED MAGNETS MADE FROM HDDR POWDERS[J].Journal of Applied Physics,1996(8 Pt.2a):5040-5044. |
[2] | Croat J J .Current status and future outlook for bonded neodymium permanent magnets (invited)[J].Journal of Applied Physiology,1997,81:4804. |
[3] | Panchanathan V;McMullen A T;Croat J J et al.Properties of bonded anisotropic magnets[J].Journal of Applied Physics,1991,70:6465. |
[4] | Tokita M.Trends in advanced SPS systems and FGM technology NEDO[A].Tokyo,Japan,1999:23-33. |
[5] | Yamazaki K .PAS (Plamasa Actived Sintering):Transient Sintering Procece Cotrol for Rapid Cosolidation of Powers[J].Journal of Materials Processing Technology,1996,56:955-965. |
[6] | Yue M;Zhang J X;Liu W Q et al.Chemical stability and microstructure of NdFeB magnets prepared by spark plasma sintering[J].Journal of Magnetism and Magnetic Materials,2004,271:364-368. |
[7] | ZHANG Jiuxing;YUE Ming;WANG Gongping.Properties of NdFeB magnets prepared by Spark Plasma Sintering[A].Newark,Delareware,USA,2002:345-353. |
[8] | 周寿增;董清飞.超强永磁体[M].北京:冶金工业出版社,2004 |
[9] | 李涛,岳明,张久兴,王公平,肖耀福,王润.Heat treatment process of new NdFeB magnet prepared by spark plasma sintering[J].中国有色金属学会会刊(英文版),2003(04):943-947. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%