采用PECVD工艺,在300℃下在50μm厚的Kapton E高分子塑料片上制备了底栅结构a-Si:H TFT阵列(20×20).用傅里叶变换红外光谱仪表征了a-Si:H薄膜的结构,用二探针法和四探针法分别表征了a-Si:H薄膜和n+a-Si:H薄膜的电导率.a-Si:H薄膜中的H(原子数分数)约为15.6%,H主要以SiH和SiH2基团的形式存在,其电导率为8.2×10-7～8.8×10-6 S/cm;n+a-Si:H薄膜的电导率为3.8×10-3 S/cm.所制备的TF工具有以下性能:Ioff≈1×10-14 A,Ionn≈1×10-9 A,Ion/Ioff≈105,Vth≈5 V,μ≈0.113cm2/(V·s),S≈2.5 V/dec,满足TFT-LCD等平板显示器件的开关寻址电路要求.
参考文献
| [1] | MacDonald W A,Looney M K,Mackerron D,et al.Latest advances in substrate for flexible electronics[J].J.SID,2007,15(12):1075-1083. |
| [2] | Gleskova H,Wagner S,Suo Z.a-Sit H TFT made on polyimide foil by PECVD at 150 ℃[J].Flat Panel Display Material,1998,508:73-78. |
| [3] | Raupp G B,Shawn M O,Moyer C,et al.Low-temperature amorphous-silicon backplane technology development for flexible displays[J].J.SID,2007,15(7).445-454. |
| [4] | Kim J H,Oh E Y,Ahn B C,et al.Performance improvement of a-Si:H TFT with SiO2 insulator by N2 plasma treatment[J].Appl.Phys.Lett.,1994,64(6):775-776. |
| [5] | Gallezot J D,Martin S,Kanicki J.Photosensitivity of a-Si:H TFT[C]//Asia Display/IDW01,Nagoya,Japan:SID,2001:407-410. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%