利用Ansys有限元软件,采用纤维随机分布模型,对在环境温度t=80℃、相对湿度RH=90%条件下的芳纶纤维/环氧树脂复合材料吸湿后的水分分布进行了模拟计算,计算结果与从材料吸湿实验中所得到的结果基本一致.根据模拟计算得到的水分浓度场对复合材料内部的吸湿应力进行了研究.结果表明:有限元方法可以比较准确地模拟复合材料在湿热环境下的水分吸收过程;复合材料内的水分浓度随老化时间延长而增大,吸湿应力也随之升高,在纤维和基体界面处的应力最大,可达50 MPa以上.
参考文献
| [1] | Pavankiran Vaddadi;Toshio Nakamura;Raman P. Singh .Inverse analysis for transient moisture diffusion through fiber-reinforced composites[J].Acta materialia,2003(1):177-193. |
| [2] | 过梅丽,肇研,谢令.航空航天结构复合材料湿热老化机理的研究[J].宇航材料工艺,2002(04):51-54. |
| [3] | Pavankiran Vaddadi;Toshio Nakamura;Raman P. Singh .Transient hygrothermal stresses in fiber reinforced composites: a heterogeneous characterization approach[J].Composites, Part A. Applied science and manufacturing,2003(8):719-730. |
| [4] | Hahn H T;Kim R Y.Swelling of composite laminates[A].Philadelphia,PA:American Society for Testing and Materials,2008:98-120. |
| [5] | Collings T A;Stone D E W.Hygrothermal effects in CFRP laminates:strains induced by temperature and moisture[A].,2005:307-316. |
| [6] | 蒋海华,马孝松.SiP器件回流焊时湿热应力的分析[J].电子元件与材料,2009(01):56-59. |
| [7] | 顾怡.FRP疲劳累积损伤理论研究进展[J].力学进展,2001(02):193-202. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%