采用MPMR合成技术得到了低黏度、高韧性、耐高温异构聚酰亚胺树脂,该树脂预浸液常温储存期大于两个月,亚胺化后纯树脂在320℃熔体黏度<300 Pa·S,树脂浇铸体的弯曲强度>100 MPa,弯曲模量>3.0 GPa,抗拉强度可达80 MPa,断裂伸长率可达6%,固化后T5d>500℃,其中PI-4复合材料在300℃的弯曲强度保持率达到76.5%.
参考文献
| [1] | 丁孟贤.聚酰亚胺-化学、结构与性能的关系及材料[M].北京:科学出版社,2006:1-7. |
| [2] | Hergenrother P M .The use,design,synthesis,and properties of high performance/high temperature polymers:A overview[J].High Performance Polymers,2003,15(01):3 -45. |
| [3] | Pater R H .Thermosetting polyimides:A review[J].SAMPE Journal,1994,30(05):29-38. |
| [4] | Meador MA. .Recent advances in the development of processable high-temperature polymers [Review][J].Annual review of materials research,1998(0):599-630. |
| [5] | 陈祥宝.高性能树脂基体[M].北京:化学工业出版社,1999:146-189. |
| [6] | Serafini T T;Devlvigs P;Lightsey G R et al.Thermoally stable polyimides from solutions of monomeric reactants[J].Journal of Applied Polymer,1972,16:905 -915. |
| [7] | Wilson D .PMR-15 processing properties and problems -A review[J].British Polymer Journal,1998,20:405-416. |
| [8] | Meyer G W;Glass T E;Grubbs H J et al.Synthesis and characterization of polyimides endcapped with phenylethynyl anhydride[J].Journal of Polymer Science Part A:Polymer Chemistry,1995,33:2141 -2 149. |
| [9] | Paul M.Hergenrother .Composites for high speed civil transports[J].SAMPE Journal,1999(1):30-32. |
| [10] | 王震,杨慧丽,益小苏,丁孟贤.苯炔基封端的联苯型聚酰亚胺复合材料[J].复合材料学报,2006(03):1-4. |
| [11] | 王震,杨慧丽,孟祥胜,高连勋,丁孟贤.苯炔基封端的异构聚酰亚胺树脂[C].第十四届全国复合材料学术会议论文集(上),2006:252-253. |
| [12] | Hergenrother P M;Connell J W;Smith J G .Phenylethynyl eontaining imide oligomers[J].Polymer,2000,41:5 073 - 5 081. |
| [13] | Hergenrother P M;Bryant B G et al.Phenylethynyl-terminated imides oligomers and polymers therfrom[J].Journal of Polymer Science Part A:Polymer Chemistry,1994,32:3 061-3 067. |
| [14] | Connell John W;Smith Jr Joseph G;Hergenrother Paul M;Rommel Monica L .Neat resin, adhesive and composite properties of reactive additive/PETI-5 blends[J].High performance polymers,2000(2):323-333. |
| [15] | Smith Jr J G;Connell J W;Hergenrother P M.High temperature transfer molding resins[A].,2000:1584 - 1 597. |
| [16] | Mengxian Ding .Isomeric polyimides[J].Progress in Polymer Science,2007(6):623-668. |
| [17] | 王震;吴雪娥;丁孟贤 等.2,3,3',4'-联苯四甲酸二酐及其衍生物的制备方法[P].专利号,03105026.3 |
| [18] | 王震;高连勋;丁孟贤 .4-苯乙炔苯酐的制备方法[P].专利号,2003101 15829.8 |
| [19] | Hergenrother P M .Poly (phenylquinexalines) containing phenylethynyl-groups[J].Macromolecules,1981,14:898 -904. |
| [20] | Hergenrother P M;Smith Jr J G .Chemistry and properties of imide oligomers end-capped with phenylethynylphthalic anhydrides[J].Polymer,1994,35(22):4 857 -4 864. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%