采用Gleeble-1500热模拟机研究了TC11合金在800～1 050℃、应变速率0.005～5/s条件下的高温变形行为.根据动力学分析,确定了不同温度区间的热激活能和热变形方程.结合变形微观组织观察确定了TC11合金的高温变形机制.结果显示:TC11合金在(α+β)两相区和β相区的热变形激活能分别为285.38和141.98 kJ/mol,表明不同温度区间的热变形机理不同;在两相区变形主要发生片状组织的球化,在β相区变形时低应变速率下(0.005～0.05/s)主要发生β相的动态再结晶,高应变速率下(0.05～5/s)主要发生动态回复.研究结果为确定该合金的最佳变形工艺参数提供了理论依据.
参考文献
| [1] | 飞机结构用TC11钛合金异型锻件的组织与性能[J].钛工业进展,2005(05):37-40. |
| [2] | 唐光昕,朱张校.TC11合金在不同热处理条件下的显微组织分析[J].稀有金属,2002(02):146-148. |
| [3] | 孙新军,白秉哲,顾家琳,陈南平.TC11合金热变形行为及Z-D关系的研究[J].稀有金属,2000(03):171-177. |
| [4] | 冯斌,王忠堂,张士宏,杨小红.TC11钛合金的高温变形力学行为[J].沈阳理工大学学报,2006(06):68-71. |
| [5] | 吴静,鲁世强,刘志和,王克鲁.TC11钛合金的热态变形行为研究[J].南昌航空工业学院学报（自然科学版）,2006(02):29-33. |
| [6] | 朱磊,张麦仓,董建新,庞克昌.TC11合金本构关系的建立及其在盘件等温锻造工艺设计中的应用[J].稀有金属材料与工程,2006(02):253-256. |
| [7] | Semiatin SL;Weiss I;Seetharaman V .Flow behavior and globularization kinetics during hot working of Ti-6Al-4V with a colony alpha microstructure[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(2):257-271. |
| [8] | Seshacharyulu T;Medeiros S C;Frazier W G et al.Hot working of commercial Ti-6AI-4V with an equiaxed α-β mierostructure:materials modeling considerations[J].Materials Science and Engineering A,2000,284(1-2):184-194. |
| [9] | Whittenberger J D .The influence of grain size and composition on slow plastic flow in Fe-Al between 1 100 and 1 400K[J].Materials Science and Engineering A,1986,77:103-106. |
| [10] | Jiantao Liu;Hongbing Chang .Investigation on hot deformation behavior of AISI T 1 high-speed steel[J].Materials Characterization,2000(3):175-186. |
| [11] | Prasad YVRK.;Seshacharyulu T. .Processing maps for hot working of titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):82-88. |
| [12] | 周军,曾卫东,舒滢,周义刚.应用热加工图研究TC17合金片状组织球化规律[J].稀有金属材料与工程,2006(02):265-269. |
| [13] | Pololer J P;关德林.晶体的高温塑性变形[M].大连:大连理工大学出版社,1989 |
| [14] | Weiss I.;Semiatin SL. .Thermomechanical processing of beta titanium alloys - an overview[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):46-65. |
| [15] | Medeiros S C;Prasad Y V R K;Frazier W G et al.Microstruetural modeling of metadynamic recrystallization in hot working of IN 718 superalloy[J].Materials Science and Engineering A,2000,293(1-2):198-207. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%