通过研究T300/5405和T300/NY9200复合材料以及基体树脂5405和NY9200的浇注料在80℃水浸中的吸水动力学、红外光谱、动态力学性能和表面形态的变化,分析了复合材料的湿热老化机理.结果表明:在80℃水浸的加速湿热老化条件下,两种复合材料的老化机理主要是吸入水分对基体的塑化/溶胀作用以及因树脂与纤维湿膨胀的不匹配所产生的内应力引起的微观开裂.
参考文献
| [1] | 过梅丽,肇研,许凤和,陈新文,李晓骏.先进聚合物基复合材料的老化研究--Ⅰ.热氧老化[J].航空学报,2000(Z1):62-65. |
| [2] | Wolff E G;Lee Stuart M.Polymer matrix composites:moisture effects and dimensional stability international encyclopedia of composites[M].VCH Publishers,Inc.New York,1990:279-323. |
| [3] | Adams R D;Singh M M.The dynamic properties of fiber-reinforced polymers exposed to hotwet conditions[M].Composites Science and Technology,1996:977-997. |
| [4] | Zhou J;Lucas J P .The effects of a water environment on anomalous absorption behavior in graphite/epoxy composites[J].Composites Science and Technology,1995,53:57-64. |
| [5] | Paplham WP.;Salin IM.;Seferis JC.;Brown RA. .ABSORPTION OF WATER IN POLYIMIDE RESINS AND COMPOSITES[J].Journal of Applied Polymer Science,1995(2):133-137. |
| [6] | 蓝立文.高分子物理[M].西安:西北工业大学出版社,1993:7778. |
| [7] | Struik L C E.Physical aging in amorphous polymers and other materials[M].Elsevier:Amsterdam,1978 |
| [8] | Morgan R L.[A].VCH Publishers,Inc. New York,1990:15-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%