使用Raman显微技术(Raman microscopy)研究了SiC纤维增强碳化硅、JG6玻璃和Pyrex玻璃复合材料界面的微观结构.研究表明,复合材料的制造过程使纤维内自由碳颗粒的大小增大,尤其是在界面层两种玻璃基复合材料制造过程使原纤维富含SiO2的表面层消失,而且发生了界面层碳结构的有序化.
参考文献
| [1] | Prewo K M;Brennan J J .[J].Journal of Materials Science,1982,17(04):1201-1206. |
| [2] | Brennan J J;Prewo K M .[J].Journal of Materials Science,1982,17(08):2371-2383. |
| [3] | Veltri R D;Condit D A;Galasso F S .[J].Journal of the American Ceramic Society,1989,72(02):478-482. |
| [4] | Lewis M H;Murthy V S R .[J].Journal of Computer Science and Technology,1991,42(1-3):221-229. |
| [5] | Bleay S M;Scott V D .[J].Journal of Materials Science,1991,26(08):2229-2239. |
| [6] | Yang X;Young R J .[J].Journal of Materials Science,1993,28(09):2536-2542. |
| [7] | Yang X;Young R J .[J].British Ceramic Transactions,1994,93(01):1-10. |
| [8] | Wang Yiming;Yang Xugang;Wang Yong .[J].J China Textile University(English Edition),1997,14(04):13-17. |
| [9] | Sasaka Y;Nishina Y;Soto M .[J].Journal of Materials Science,1987,22(02):443-448. |
| [10] | Schreck P H;Vix-Guteri C;Ehrburger P .[J].Journal of Materials Science,1992,27(15):4237,4243-4246. |
| [11] | Maniettend Y;Berlin O .[J].Journal of Materials Science,1989,24(09):3361-3370. |
| [12] | Tuinstra E;Koenig J I .[J].Journal of Chemical Physics,1970,53(03):1126-1130. |
| [13] | Chien C;Dresselhans O;Endo M .[J].Physical Review,1982,26(12):5867-5870. |
| [14] | Fitzer B;Ganter E;Rozploch F .[J].High Temperature and High Pressure,1987,9(05):537-544. |
| [15] | Yang Xugang;Bannister D J;Young R J .[J].Journal of the American Society,1996,79:1868-1875. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%