采用腐蚀浸泡、电化学极化曲线、交流阻抗以及X射线衍射等方法,对电沉积Zn和Zn-Al复合镀层的耐蚀性能进行了比较研究.结果表明:Zn-Al复合镀层在5%NaCl溶液和10%HCl溶液中比Zn镀层具有更好的耐蚀性能;电化学极化和交流阻抗测试表明Zn-Al复合镀层的腐蚀电流密度减小,极化电阻和交流阻抗增大,腐蚀速率小于Zn镀层;Zn-Al复合镀层呈现(002)晶面高程度择优,是使其耐蚀性提高的主要原因.
参考文献
| [1] | Kondo K.;Obgishi A. .Electrodeposition of Zinc-SiO_2 Composite[J].Journal of the Electrochemical Society,2000(7):2611-2613. |
| [2] | Gomes A;Pereira MID;Mendonca MH;Costa FM .Zn-TiO2 composite films prepared by pulsed electrodeposition[J].Journal of solid state electrochemistry,2005(4):190-196. |
| [3] | 骆心怡,何建平,李顺林.电沉积CeO2/Zn纳米复合涂层[J].南京航空航天大学学报(英文版),2002(02):161-165. |
| [4] | Zhang Y;Fan Y;Yang X .The process and mechanism of electrodeposition Zn-Fe-SiO2 composite coating[J].Plating and Surface Finishing,2004,91(09):39-43. |
| [5] | 王云燕,彭文杰,柴立元,舒余德.Electrochemical behaviors of Zn-Fe alloy and Zn-Fe-TiO2 composite electrodeposition[J].中南工业大学学报(英文版),2003(03):183-189. |
| [6] | Yoshihara T;Kimura H;Harada S .Study of high corrosion resistant zinc-aluminum composite electroplated steel sheet[J].Journal of the Iron & Steel Institute of Japan,1980,66(07):779-789. |
| [7] | 刘永辉.电化学测试技术[M].北京:北京航空航天大学出版社,1987:360-361. |
| [8] | 亚当森 A W.表面的物理化学[M].北京:科学出版社,1984:257. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%