利用热重分析法、X射线衍射法和扫描电镜研究了不同石墨含量(0%、3%、6%、9%)镍铬基高温合金在800 ℃、900 ℃和950 ℃下的高温氧化行为.合金在石墨含量较低,800 ℃、900 ℃氧化时,氧化增重基本遵循抛物线规律,表面氧化膜无剥落,在950 ℃氧化时表面氧化膜出现剥落,近似直线规律.900 ℃氧化时,含石墨0%、3%的合金氧化膜由Cr2O3和NiCr2O4组成.根据氧化膜的组成分析了合金的氧化机理.
参考文献
| [1] | 朱日彰;何业东;齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995 |
| [2] | Xiang J H;Gesmundo F;Niu Y .The oxidation of two ternary Ni-Cu-10at%Al alloys in 1 atmof pure O2 at 800～900 ℃[J].Corrosion Science,2004,46:2025-2039. |
| [3] | Bapu GNKR;Jayakrishnan S .Oxidation characteristics of electrodeposited nickel-zirconia composites at high temperature[J].Materials Chemistry and Physics,2006(2/3):321-325. |
| [4] | A Morales-Rodrguez;A Bravo-Leon;G Richter et al.Influence of oxidation on the high-temperature mechanical properties of zirconia/nickel cermets[J].Scripta Materialia,2006,54:2087-2090. |
| [5] | Huang L;Sun XF;Guan HR;Hu ZQ .Effect of rhenium addition on isothermal oxidation behavior of single-crystal Ni-based superalloy[J].Surface & Coatings Technology,2006(24):6863-6870. |
| [6] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%