分析了硫化氢腐蚀钢材的原理,针对耐硫化氢腐蚀环境,就合金元素及微合金化、控制轧制对低合金高强度钢组织及性能的影响进行论述,提出了耐硫化氢腐蚀的低合金高强度钢的设计思路.
参考文献
| [1] | Ma Houyi;Cheng Xiaoliang;Li Guiqiu.The influence of hydrogen sulfide on corrosion of iron under differet conditions[J].Corrosion,2000(42):1669-1683. |
| [2] | Vedage H;Ramanarayanan T A;Mumford J D et al.Electrochemical growth of Iron sulfide films in H2S saturated chloride media[J].Corrosion,1993,49(02):114-121. |
| [3] | Y. -M. Wu .Applying process modeling to screen refining equipment for wet hydrogen sulfide service[J].Corrosion: The Journal of Science and Engineering,1998(2):169-173. |
| [4] | Kimura M et al.Sulfide stress cracking of line pipe[J].CORROSION,1989,45(04):340-346. |
| [5] | H.H.Huang .Electrochemical Behavior of A516 Carbon Steel in Solutions Containing Hydrogen Sulfide[J].Corrosion: The Journal of Science and Engineering,1996(9):708-713. |
| [6] | 徐增华.金属耐蚀材料[J].腐蚀与防护,2001(01):46-48. |
| [7] | 高惠临.管线钢--组织、性能、焊接行为[M].西安:陕西科学技术出版社,1995 |
| [8] | Cayard M S.Research report on characterization and monitoring of cracking in wet H2S service[A].WRC Bulletin,1994:396. |
| [9] | 徐克彬,刘猛,刘文启.含硫化氢井试油工艺研究[J].油气井测试,1995(02):52-57. |
| [10] | 赵平.H2S腐蚀的影响因素（Ⅱ）[J].全面腐蚀控制,2002(03):8-9. |
| [11] | Snape E .Roles of composition and microstructure in sulfide cracking of stssl[J].Corrosion,1968,24(09):261-282. |
| [12] | 李长荣.抗H2S应力腐蚀用钢30CrMoVTiAl的力学性能[J].贵州工业大学学报,1997(06):21. |
| [13] | Stratmann J;Grobner P J .Металловедениеитер,обр[J].металлов,1977,7:60. |
| [14] | 何建宏;唐祥云;陈南平 .铁素体-奥氏体不锈钢氢致开裂研究[J].金属学报,1989,25(01):37. |
| [15] | 莫德敏;杨海林 .微合金元素对改善高强度低合金钢抗氢诱导裂纹的作用[J].宽厚板,1998,4(06):20-25. |
| [16] | 东涛 .石油天然气长输管线用钢研究进展[J].焊管,1995,18(06):7-12. |
| [17] | Fraser J P;Elderdge G G;Treseder R S .Laboratory and field methods for quantitative study of sulfide corrosion cracking[J].Corrosion,1958,14(11):37-44. |
| [18] | Treseder R S;Swanson T M .Factors in sulfide corrosion cracking of high strength steels[J].Corrosion,1968,24(02):31-37. |
| [19] | 王青江;王仪康 .微合金控制轧制钢[J].焊管,1994,17(04):14-20. |
| [20] | 薛小怀,华永成,郑惠锦,詹水强,钱百年,楼松年.高强钢的超低碳微合金化[J].造船技术,2004(01):26-29. |
| [21] | 赵明纯,肖福仁,单以银,李玉海,杨柯.超低碳针状铁素体管线钢的显微特征及强韧性行为[J].金属学报,2002(03):283-287. |
| [22] | Devletian J H;Singh D;Wood We.Welding of HSLA-100 steel using ultralowcarbon bainitic weld metal to eliminate reheating in ASM[A].,1995:341-346. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%