对T700/9368光滑板及两种孔径的含孔层合板进行了拉-拉疲劳试验,测量试件刚度随加载周期的衰减规律,并利用超声波C扫描和破坏断口分析方法,对T700复合材料的疲劳损伤机理进行分析.根据弹性模量法建立了层合板疲劳累积损伤模型,并从平均应力准则概念出发,建立了含孔层合板的疲劳累积损伤模型.将试验数据运用最小二乘法拟合后代入疲劳损伤模型,得到T700/9368光滑板及含孔板疲劳寿命的具体计算公式,应用公式预测了在不同应力水平下的层合板疲劳寿命,与试验结果的吻合良好.
参考文献
| [1] | RADHAKRISHNAN K .Fatigue and reliability evaluation of unnotched carbon epoxy laminates[J].Comp Mat,1984,10(01):21-31. |
| [2] | YANG J N .Residual strength degradation model and theory of periodic proof tests for graphite pepoxy laminates[J].Journal of Composite Materials,1977,11(04):177-197. |
| [3] | STINCHCOMB.Nondestructive evaluation of damage accumulation processes in composite laminates[J].Journal of Computer Science and Technology,1986(25):103-118. |
| [4] | PAUL .A damage accumulation in graphite/epoxy laminates due to cycilc gadient stress fields[J].Rein Plas &Comp,1993,12(10):111-116. |
| [5] | 齐红宇,温卫东.先进纤维增强复合材料疲劳寿命的预测[J].纤维复合材料,2001(02):3-6. |
| [6] | 齐红宇,温卫东,崔海涛.含孔复合材料层合板疲劳寿命预测研究[J].航空动力学报,2003(05):658-661. |
| [7] | BADALIANE R;DILL H D.Damage in composite materials[J].ASTM STP775,1982(06):229. |
| [8] | LEMAITRE J.Evolution of dissipation and damage in metals,submitted it dynamic loading[A].Kyoto.Japan,1968 |
| [9] | 程光旭,韦玮,李光哲.复合材料疲劳损伤演化的两阶段模型[J].机械工程材料,2000(05):1-4. |
| [10] | 徐颖,温卫东,崔海坡.含冲击损伤复合材料层合板疲劳试验研究[J].宇航材料工艺,2007(02):73-76,80. |
| [11] | 陈祥宝.聚合物基复合材料手册[M].北京:化学工业出版社,2004:54-56,73. |
| [12] | 杨光松.损伤力学与复合材料损伤[M].北京:国防工业出版社,1995:132-135. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%