以大粒度Ti-45Al-8.5Nb-0.2B-0.2W-0.1Y预合金粉末为原料,研究了高能球磨与无压烧结制备高铌TiAl合金工艺.结果表明高能球磨可显著改善合金粉末的压制性能,并对粉末的烧结致密化有促进作用;高能球磨60min的预合金粉末经过1500℃,2h无压烧结后,可获得高致密度、具有细小全层片组织的高铌TiAl合金,其抗压强度为3150MPa,相对压缩率为25.2%,显示出较好的室温压缩性能.
参考文献
| [1] | CHE G L;ZHANG W J;WANG Y.Ti-Al-Nb intermetallic alloys based on the ternary intermetallic compound[A].Warrendale PA USA:TMS,1993:319-324. |
| [2] | YOSHINARA M;MIURA K .Effect of Nb on oxidation behavior of TiAl[J].Intermetallics,1995,3(05):357-363. |
| [3] | CHEN G L;LIN J P;SONG X P.Development of high Nb containing high temperature TiAl alloys[A].Warrendale PA USA:TMS,2004:153-166. |
| [4] | CHEN G L;ZHANG W J;LIU Z C.Microstructure and properties of high-Nb containing TiAl-based alloys[A].Warrendale PA USA:TMS,1999:371-380. |
| [5] | J.D.H.Paul;F.Appel;R.Wagner .The compression behaviour of niobium alloyed γ-titanium aluminides[J].Acta materialia,1998(4):1075-1085. |
| [6] | J.Moll;B.McTiernan .PM TiAl alloys: the sky's the limit[J].Metal Powder Report,2000(1):18-22. |
| [7] | YOLTON C F;KIM Y W;HABEL U.Powder metallurgy processing of gamma titanium aluminide[A].Warrendale PA USA:TMS,2003:233-240. |
| [8] | WANG G X;DAHMS M .An overview:TiAl-based alloys prepared by elemental powder metallurgy[J].Powder Metallurgy International,1992,24(04):219-225. |
| [9] | Han Seo Cho;Soo Woo Nam;Sun-Keun Hwang;Nack J. Kim .TENSILE CREEP DEFORMATION AND FRACTURE, BEHAVIORS OF THE LAMELLAR TiAl ALLOY OF ELEMENTAL POWDER METALLURGY[J].Scripta materialia,1997(11):1295-1301. |
| [10] | YOLTON F;HABEL U;KIM Y W.Processing,microstructures and mechanical properties of PM gamma titanium aluminide[A].Warrendale PA USA:TMS,2004:215-228. |
| [11] | HABE U;DAS G;YOLTON F.Processing,microstructure and tensile properties of,gamma-TiAl PM alloy 395MM[A].Warrendale PA USA:TMS,2003:297-304. |
| [12] | 王衍行,赵丽明,林均品,王艳丽,曲选辉,陈国良.高Nb-TiAl合金粉的制备及其特性[J].航空材料学报,2007(05):34-39. |
| [13] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1997:173-194. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%