采用OM,XRD,XRF,SEM,EPMA,TEM等分析手段研究了稀土Y对Ti-23Al-25Nb合金显微组织的影响.结果表明:两种合金铸态显微组织均为O相;稀土Y明显细化了Ti-23Al-25Nb合金晶粒尺寸,Ti-23Al-25Nb合金的晶粒尺寸在400～600μm之间,Ti-23Al-25Nb-0.36Y合金的晶粒尺寸在40～100μm之间,细化大约6～8倍.通过Ti-23Al-25Nb-0.36Y合金背散射、各元素线分布和TEM分析发现,稀土Y在Ti-23Al-25Nb合金中以Y2O3的形式存在于晶内和晶界,根据O相形成机制和晶粒细化理论,分析了稀土Y细化O相晶粒的过程.
参考文献
| [1] | BANERJEE D;GOGIA A K;NANDY T K et al.A new ordered orthorhombic phase in a Ti3Al-Nb alloy[J].Acta Materialia,1988,36(04):871-882. |
| [2] | GOGIA A K;NANDY T K;BANERJEE D et al.Microstructure and mechanical properties of orthorhombic alloys in the Ti-Al-Nb system[J].Intermetallics,1998,6(7-8):741-748. |
| [3] | CHU F;MITCHELL T E;MAJUMDAR B et al.Elastic properties of the O phase in Ti-Al-Nb alloys[J].Intermetallics,1997,5(02):147-156. |
| [4] | Y.Mao;S.Li .Microstructure and tensile properties of orthorhombic Ti-Al-Nb-TA alloys[J].Intermetallics,2000(5/6):659-662. |
| [5] | ROWE R G .Ti2AlNb based alloys outperform conventional titanium aluminides[J].Current Advances in Materials and Processes,1992,3:33-35. |
| [6] | 吴波 .Ti<,2>AlNb基合金的制备工艺、组织和力学性能研究[D].北京有色金属研究总院,2002. |
| [7] | 张永刚;韩雅芳;陈国良.金属间化合物结构材料[M].北京:国防工业出版社,2001:789-797. |
| [8] | 铸造合金材料及凝固编委会.铸造合金材料及凝固[M].北京:冶金工业出版社,2001:3-21. |
| [9] | 孔凡涛,董孟环,陈玉勇.Ti-47Al-1.2Ce合金显微组织及稀土相[J].中国稀土学报,2002(01):72-73. |
| [10] | 武英 .Ti<,3>Al-Nb合金的显微组织与拉伸变形断裂行为[D].哈尔滨工业大学,1997. |
| [11] | BENDERSKY L A;ROYTBURD A;BOETTINGER W J .Phase transformations in the(Ti,Al)3Nb section of the Ti-Al-Nb system-I,microstructural predictions based on a subgroup relation between phases[J].Acta Metallurgica Et Materialia,1994,42(07):2323-2335. |
| [12] | 孔凡涛 .稀土对TiAl合金凝固组织及性能影响的研究[D].哈尔滨:哈尔滨工业大学,2003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%