对TC11钛合金经不同温度和时间热暴露后的拉伸性能进行了考察,对不同热暴露后断裂行为的变化及其原因进行了分析研究.结果表明,热暴露温度不高于550℃,热暴露后的室温拉伸性能与未处理时相差不大,断面由纤维区和剪切唇区组成,无放射区;热暴露温度高于550℃时,热暴露后TC11钛合金的塑性急剧下降,断面由放射区和剪切唇区组成,无纤维区,且放射区收敛于断面上靠近试样表面附近,点源.放射区微观上可见韧窝、准解理及沿相界、晶界分离的混合形貌特征,不同于纤维区的等轴韧窝形貌,且剪切唇区可见解理、准解理脆性断裂特征.热暴露后TC11钛合金这种宏微观断裂行为的变化是由试样表面氧污染层的缺口效应、针状α2(Ti3Al)相的析出以及次生α与β的长大所致.
参考文献
| [1] | DOLINSKAIA L K;GUSEVALN.Effectof small of oxygen impurities on formation of metastable phase in alloy of titanium with vanadium[A].Mosscow,1978:226-231. |
| [2] | IMAM M A;RATH B B;GILLESPIE D J.Effect of oxygen on microstructure and properties of Ti6211 alloy[A].Munich,Germany,1984:11-16. |
| [3] | 赵永庆,朱康英,李左臣.Ti811合金的热稳定性能[J].稀有金属材料与工程,1997(03):35-39. |
| [4] | JUDY R W.Role of composition and microstructure in dynamic and static fracture of alpha-beta titanium alloys[A].San Diego,1993:233. |
| [5] | WASZ M L;GRIFFIN A G .Effect of oxygen and hydrogen on mechanical properties of commercial purity titanium[J][J].International Materials Reviews,1996,41(01):1-9. |
| [6] | ROSE R M.Electromagnetic NDE interial contamination in titanium alloy weldments[M].Cambridge,1984:173. |
| [7] | JOHNSON T J;LORETTO M H.Oxidation and creep behavior of high temperature titanium alloy[M].Titanium '92 Science and Technology[C],1993:2035. |
| [8] | 崔文芳,魏海荣,罗国珍.IMI834和Ti-1100在550℃～750℃高温下的氧化行为[J].稀有金属材料与工程,1997(02):31-35. |
| [9] | 张卫方,刘新灵,赵爱国,刘高远,陶春虎.钛合金在500℃～650℃下的氧化行为研究[J].材料热处理学报,2003(02):55-58. |
| [10] | 张卫方.钛合金的断口定量分析及环境敏感性[M].北京:北京航空材料研究院,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%