介绍和评述了阴极剥离对有机涂层劣化和涂层下金属腐蚀过程影响的研究现状,讨论了影响阴极剥离发生与发展的因素、阴极剥离作用机理和提高有机涂层耐阴极剥离的途径.同时综述了研究有机涂层阴极剥离的测试技术和研究方法.
参考文献
| [1] | Nguyen T N;Hubbard J B;McFadden G B .A mathematical model for the cathodic blistering of organic coatings on steel immersed in electrolytes[J].J Coat Technel,1991,63:43-52. |
| [2] | Guillaumin V;Landolt D .Effect of dispersion agent on the degradation of a water borne paint on steel studied by scanning acoustic microscopy and impedance[J].Corrosion Science,2002,44:179-189. |
| [3] | Hemandez M A;Galliano F;Landolt D .Mechanism of cathodic delamination control of zinc-aluminum phosphate pigment in waterborne coatings[J].Corrosion Science,2004,46:2281-2300. |
| [4] | Zin IM;Lyon SB;Hussain A .Under-film corrosion of epoxy-coated galvanised steel - An EIS and SVET study of the effect of inhibition at defects[J].Progress in Organic Coatings: An International Review Journal,2005(2):126-135. |
| [5] | Furbeth W;Stratmarm M .The delamination of polymeric coatings from electrogalvanised steel-a mechanistic approach.Part 1:delamination from a defect with intact zinc layer[J].Cortes SCi,2001,43:207-227. |
| [6] | 胡吉明,张鉴清,谢德明,曹楚南.水在有机涂层中的传输Ⅰ Fick扩散过程[J].中国腐蚀与防护学报,2002(05):311-315. |
| [7] | 胡吉明,张鉴清,谢德明,曹楚南.水在有机涂层中的传输--Ⅱ复杂的实际传输过程[J].中国腐蚀与防护学报,2002(06):371-374. |
| [8] | Bernhard Wessling;Joerg Posdorfer .Corrosion prevention with an organic metal (polyaniline): corrosion test results[J].Electrochimica Acta,1999(12):2139-2147. |
| [9] | Miszczyk A;Schauer T .Electrochemical approach to evaluate the interlayer adhesion of organic coatings[J].Progress in Organic Coatings: An International Review Journal,2005(4):298-305. |
| [10] | A. R. Nazarov;D. Thierry .Scanning Kelvin probe study of metal/polymer interfaces[J].Electrochimica Acta,2004(17/18):2955-2964. |
| [11] | Long A;Strockel H;Stratmann M .The delamination of polymeric coatings from steel Part 1.Calibration of the Kelvin probe and basic delamination mechanism[J].Corrosion Science,1999,41:547-578. |
| [12] | Leng A;Streckel H;Stratmann M .The delamination of polymeric coatings from steel Part 3.Effect of the oxygen partial pressure on the delamination reaction and current distribution at the metal/polymer interface[J].Corrosion Science,1999,41:599. |
| [13] | Leng A;Streckel H;Stratmann M .The delamination of polymeric coatings from steel Part 2.First stage of delamination,effect of type and concentration of cations on delamination,chemical analysis of the interface[J].Corrosion Science,1999,41:579. |
| [14] | Flavio Deflorian;Stefano Rossi .An EIS study of ion diffusion through organic coatings[J].Electrochimica Acta,2006(8/9):1736-1744. |
| [15] | Bierwagen G.;Tallman D.;Li JP.;He LY.;Jeffcoate C. .EIS studies of coated metals in accelerated exposure[J].Progress in Organic Coatings: An International Review Journal,2003(2):148-157. |
| [16] | Malgorzata Zubielewiez;Elzbieta Kanska-Tamawska;Antonina Kozlowska .Protective properties of organic phesphate-pigmented coatings on phosphated steel substrates[J].Progress in Organic Coatings,2005,53:276-285. |
| [17] | Grundmeier G;Rossenbeck B;Roschmann K J.Corrosion protection of Zn-phosphate containing water berne dispersion coatings Part 2.Investigations of the corrosive de-adhesion of model latex coatings on iron[J].Corrosion Science,2006 |
| [18] | Worsley D A;Williams D;Ling J S G .Mechanistic changes in cut-edge corrosion induced by variation of organic coating porosity[J].Corrosion Science,2001,43:2335-2348. |
| [19] | Q. Le Thu;H. Takenouti;S. Touzain .EIS characterization of thick flawed organic coatings aged under cathodic protection in seawater[J].Electrochimica Acta,2006(12):2491-2502. |
| [20] | Isabel C;Margarit P;Oscar R Mttos .Abeut coatings and cathodic protection:properties of the coatings influencing delamination and cathodic protection criteria[J].Electrochim Acid,1998,44:363-371. |
| [21] | Miszczyk A.;Darowicki K. .Effect of environmental temperature variations on protective properties of organic coatings [Review][J].Progress in Organic Coatings: An International Review Journal,2003(1):49-54. |
| [22] | Keehler E L .The mechanism of cathodic disbondment of protective organic coatings-aqueous displacement at elevated pH[J].Corrosion,1984,40(01):5-8. |
| [23] | M. G. S. Ferreira;R. G. Duarte;M. R. Montemor;A. M. R. Simoes .Silanes and rare earth salts as chromate replacers for pre-treatments on galvanised steel[J].Electrochimica Acta,2004(17/18):2927-2935. |
| [24] | Deflorian F;Rossi S;Fedrizzi L.Silane pre-treatments on copper and aluminium[J].Electrochim Acid,2006 |
| [25] | L. Fedrizzi;F. J. Rodriguez;S. Rossi;F. Deflorian;R. Di Maggio .The use of electrochemical techniques to study the corrosion behaviour of organic coatings on steel pretreated with sol-gel zirconia films[J].Electrochimica Acta,2001(24/25):3715-3724. |
| [26] | Zubielewicz M;Gnot W .Mechanisms of non-toxic anticorrosive pigments in organic waterborne coatings[J].Progress in Organic Coatings: An International Review Journal,2004(4):358-371. |
| [27] | G. Williams;R. J. Holness;D. A. Worsley;H. N. McMurray .Inhibition of corrosion-driven organic coating delamination on zinc by polyaniline[J].Electrochemistry communications,2004(6):549-555. |
| [28] | 刘建国,龚高平,严川伟.聚合物/达克罗复合涂层体系在3.5%NaCl中耐蚀性能的EIS研究[J].中国腐蚀与防护学报,2006(02):89-93. |
| [29] | Amirudin A;Thierry D .Application of electrochemical impedance spectroscopy to study the degradation of polymer-coated metals[J].Progress in Organic Coatings,1995,26:1-28. |
| [30] | Mirabedini SM.;Thompson GE.;Moradian S.;Scantlebury JD. .Corrosion performance of powder coated aluminium using EIS[J].Progress in Organic Coatings: An International Review Journal,2003(2):112-120. |
| [31] | Deflorian F;Fedrizzi L .Adhesion characterization of protection organic coatings by electrochemical impedance spectroscopy[J].Journal of Adhesion Science and Technology,1999,13(05):629. |
| [32] | Harnyama;Hirayara R;Haruyama S .Electrochemical impedance for degraded coated steel having pores[J].Corrosion,1991,47(12):952. |
| [33] | Mansfeld F .Determination of coating deterioration with EIS Part 1.Basic relationships[J].Corrosion,1991,47:958. |
| [34] | Mansfeld F;Tsai C H .Determination of coating deterioration with EIS Part 2.Development of a method for field testing of protective coatings[J].Corrosion,1993,49:726. |
| [35] | 高志明,宋诗哲,徐云海.涂层失效过程电化学阻抗谱的神经网络分析[J].中国腐蚀与防护学报,2005(02):106-109. |
| [36] | 王燕华,张涛,王佳,王福会.Kelvin探头参比电极技术在大气腐蚀研究中的应用[J].中国腐蚀与防护学报,2004(01):59-64. |
| [37] | Doherty M;Sykes J M .Micro-cells beneath organic lacquers:a study using scanning Kelvin probe and scanning acoustic microscopy[J].Corrosion Science,2004,46:1265-1289. |
| [38] | J. H. W. de Wit .Local potential measurements with the SKPFM on aluminium alloys[J].Electrochimica Acta,2004(17/18):2841-2850. |
| [39] | Michael Rohwerder;Elke Hornung;Martin Stratmann .Microscopic aspects of electrochemical delamination: an SKPFM study[J].Electrochimica Acta,2003(9):1235-1243. |
| [40] | Jean-Baptiste Jorcin;Emmanuel Aragon;Celine Merlatti;Nadine Pebere .Delaminated areas beneath organic coating: A local electrochemical impedance approach[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(7):1779-1790. |
| [41] | 张鉴清,张昭,王建明,曹楚南.电化学噪声的分析与应用-I.电化学噪声的分析原理[J].中国腐蚀与防护学报,2001(05):310-320. |
| [42] | 张鉴清,张昭,王建明,成少安,曹楚南.电化学噪声的分析与应用Ⅱ.电化学噪声的应用[J].中国腐蚀与防护学报,2002(04):241-248. |
| [43] | 曹发和,张昭,施彦彦,张鉴清,曹楚南.电化学噪声频谱的Vision C++实现[J].中国腐蚀与防护学报,2005(01):7-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%