应用STM原位观察在不同氯离子浓度和pH值以及加入缓蚀剂前后的模拟混凝土孔溶液中的钢筋表面微观形貌.在pH=12.40的混凝土模拟孔溶液中,钢筋表面趋向均一,钝化膜的薄弱部分得到强化;在含3.5%NaCl,pH=10.40的混凝土模拟孔溶液中由于局部腐蚀的发生,可观察到不规则的沉积物的形成、生长;LD-2型复合缓蚀剂能消除腐蚀活性,促使表面微观缺陷消亡,增加钝化膜的耐蚀能力.研究结果说明,STM可在纳米尺度上观察表面形貌变化,可成为原位研究钢筋在模拟混凝土孔溶液中腐蚀和缓蚀的动态行为的重要手段.
参考文献
| [1] | 胡艳玲,胡融刚,邵敏华,林昌健.不锈钢钝化膜形成和破坏过程的原位ECSTM研究[J].金属学报,2001(09):965-970. |
| [2] | Maurice V.;Marcus P.;Strehblow HH. .In situ STM study of the initial stages of oxidation of Cu(111) in aqueous solution[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,2000(1/3):185-194. |
| [3] | Vogt MR.;Magnussen OM.;Behm RJ.;Lachenwitzer A. .In-situ STM study of the initial stages of corrosion of Cu(100) electrodes in sulfuric and hydrochloric acid solution[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,1998(1):49-69. |
| [4] | L. Sziraki;E. Szocs;Zs. Pilbath;K. Papp;E. Kalman .Study of the initial stage of white rust formation on zinc single crystal by EIS, STM/AFM and SEM/EDS techniques[J].Electrochimica Acta,2001(24/25):3743-3754. |
| [5] | 杜荣归,王周成,黄若双,胡融刚,赵冰,谭建光,林昌健.LD-2复合缓蚀剂对海水介质混凝土中钢筋阻锈作用研究[J].电化学,2001(04):494-500. |
| [6] | 洪定海.混凝土中钢筋的腐蚀与防护[M].北京:中国铁道出版社,1998:16. |
| [7] | 中国腐蚀与防护学会;杨武;顾祥濬;黎樵燊.肖京先金属的局部腐蚀[M].北京:化学工业出版社,1993:45. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%