为了研究微量Sc对Al-3.5Cu-1.5Li-0.12Zr合金组织与性能的影响,采用铸锭冶金法,制备了4种不同Sc含量的Al-3.5Cu-1.5Li-0.12Zr合金.采用室温拉伸力学性能实验、金相显微镜和透射电镜研究了微量Sc对Al-3.5Cu-1.5Li-0.12Zr合金微观组织和拉伸性能的影响.结果表明:添加0.1%Sc能消除铸态合金的枝晶组织,有效地抑制了再结晶的发生,具有一定的强化作用和明显的增塑效应;添加O.15%Sc和0.25%Sc能显著细化合金铸态的晶粒组织,但添加0.15%Sc不能抑制合金固溶过程中再结晶;添加0.25%Sc会促进合金固溶过程中的再结晶,从而降低合金的强度.合金中较适宜的Sc加入量为0.10%～0.15%,此时合金既具有较高的强度,又兼具较好的塑性.
参考文献
| [1] | James M. Fragomeni;Robert Wheeler .The Strengthening and Microstructure of Precipitation Hardened Al-Li-Cu Alloys[J].Materials Science Forum,2003(Pt.1):309-314. |
| [2] | M. J. Starink;A. J. Hobson;I. Sinclair;P. J. Gregson .Embrittlement of Al-Li-Cu-Mg alloys at slightly elevated temperatures: microstructural mechanisms of hardening[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):130-142. |
| [3] | JOH C H;YAMADA K;MIURA Y .Effect of Sc-addition on coarsening behavior of Al3 Li precipitates in Al-Li alloys[J].MATERIALS TRANSACTIONS,1998,5(40):439-443. |
| [4] | TAN Cheng-yu,ZHENG Zi-qiao,XIA Chang-qing.The Aging Feature of Al-Li-Cu-Mg-Zr Alloy Containing Sc[J].中南工业大学学报,2000(02):65. |
| [5] | S.Iwamura;M.Nakayama;Y.Miura .Coherency between Al_3Sc Precipitate and the Matrix in Al Alloys Containing Sc[J].Materials Science Forum,2002(Pt.2):1151-1156. |
| [6] | MILMAN Y V;LOTSKO D V;SIRKO O L .Sc effect of improving mechanical properties in aluminum alloys[J].Materials Science Forum,2000,331-337:1107-1112. |
| [7] | Zhimin Yin;Qinglin Pan;Yonghong Zhang;Feng Jiang .Effect of minor Sc and Zr on the microstructure and mechanical properties of Al-Mg based alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1):151-155. |
| [8] | NORMAN A F;PRANGNELL P B;MCEWEN R S .The solidification behaviour of dilute aluminum alloys[J].ACTA MATERIALIA,1998,16(46):5715-5732. |
| [9] | 潘青林,尹志民,邹景霞,陈显明,张传福.微量Sc在Al-Mg合金中的作用[J].金属学报,2001(07):749-753. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%