为提高Ti/SnO2电极的电催化性能,采用溶胶-凝胶法,并结合高温热处理工艺制备了钛基SnO2纳米涂层电催化电极.以苯酚为目标污染物,考察了所制备电极的电催化性能,并采用XRD、SEM、XPS等方法研究了制备的SnO2纳米涂层电极的表面形貌、晶粒粒径、元素组成和表面元素的化学环境等.研究结果表明:由于纳米涂层具有较大的比表面积,使得所制备电极的性能较非纳米涂层的钛基二氧化锡电极大为提高,完全降解等量苯酚所需时间减少了33.3%.电极表面主要是四方相金红石结构的SnO2晶体,粒径在10 nm以下.
参考文献
| [1] | FENG Y J;LI X Y.Electrochemical degradation of phenol:performance of several metal oxide-based anodes[A].Washington DC,2001:25-29. |
| [2] | KOTZ R;STUCKI S;CARCER B .Electrochemical waste water treatment using high overvoltage anodes.Part Ⅰ.physical and electrochemical properties of SnO2anodes[J].Journal of Applied Electrochemistry,1991,21(01):14-20. |
| [3] | Zanta CLPS.;Michaud PA.;Comninellis C.;De Andrade AR.;Boodts JFC. .Electrochemical oxidation of p-chlorophenol on SnO2-Sb2O5 based anodes for wastewater treatment[J].Journal of Applied Electrochemistry,2003(12):1211-1215. |
| [4] | COMNINELLIS C;BATTISTI D .Service life of Ti/SnO2 -Sb2O5 anodes[J].Journal of Applied Electrochemistry,1997,27(08):970-974. |
| [5] | 冯玉杰,沈宏,崔玉虹,刘峻峰.钛基二氧化铅电催化电极的制备及电催化性能研究[J].分子催化,2002(03):181-186. |
| [6] | Y.J. Feng;X.Y. Li .Electro-catalytic oxidation of phenol on several metal-oxide electrodes in aqueous solution[J].Water research: A journal of the international water association,2003(10):2399-2407. |
| [7] | 崔玉虹,冯玉杰,刘峻峰.含Mn中间层钛基二氧化锡电催化电极的性能[J].材料研究学报,2005(01):47-53. |
| [8] | 冯玉杰,崔玉虹,孙丽欣,刘峻峰,蔡伟民.电化学废水处理技术及高效电催化电极的研究与进展[J].哈尔滨工业大学学报,2004(04):450-455. |
| [9] | 尤宏,崔玉虹,冯玉杰,刘峻峰,蔡伟民.钛基Co中间层SnO2电催化电极的制备及性能研究[J].材料科学与工艺,2004(03):230-233. |
| [10] | 国家环保局.水和废水监测分析方法[M].北京:中国环境科学出版社,1997 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%