为了研究等通道转角挤压等规聚丙烯的挤压工艺条件、结构与性能之间的关系,采用90°转角模具及挤压路径A、在熔点以下的160℃制备了不同挤压次数的等规聚丙烯样品,利用广角X射线衍射(WAXD)、差示扫描量热分析(DSC)等手段对其结构进行表征.结果表明,随挤压次数增加,等规聚丙烯分子取向明显增加,材料结晶度提高,试样的力学性能提高十分显著,未挤压试样的抗拉强度为17.13 MPa,经过三次挤压后,抗拉强度提高到59.38 MPa.
参考文献
| [1] | Weiler W.;Gogolewski S. .ENHANCEMENT OF THE MECHANICAL PROPERTIES OF POLYLACTIDES BY SOLID-STATE EXTRUSION .1. POLY(D-LACTIDE)[J].Biomaterials,1996(5):529-535. |
| [2] | ZHIYONG XIA;HUNG-JUE SUE;ALEX J.HSIEH .Impact Fracture Behavior of Molecularly Orientated Polycarbonate Sheets[J].Journal of Applied Polymer Science,2001(11):2060-2066. |
| [3] | Gurhan Kalay;Rui A.Sousa;Rui L.Reis;Atonio M.Cunha;Michael J.Bevis .The Enhancement of the Mechanical Properties of a High-Density Polyethylene[J].Journal of Applied Polymer Science,1999(12):2473-2483. |
| [4] | RAWSON Keith W;ALLAN Peter S .Controlled Orientation of Retlective Pigment and Optical Property Characterization of Injection-Molded Polypropylene[J].Polymer Engineering and Science,1999,39(01):50-57. |
| [5] | LI C K;SUE H J .Novel equal channel angular extrusion process for improving physical and mechanical properties in polymer[J].Polymeric Preprints(American Chemical Society Division of Polymer Chemistry),1998,39:728-729. |
| [6] | 马玉春,崔宏祥.等通道转角挤压对PA1010结晶结构和力学性能的影响[J].塑料工业,2003(09):21-22,28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%