研究氢对TA16钛合金显微组织、氢脆行为和应力腐蚀行为的影响,以及TA16钛合金在8.5 MPa高温碱性水中的吸氢性能.结果表明,氢在TA16钛合金中形成面心立方的8相氢化物TiHx(x=1～2).在室温条件下,TA16钛合金氢脆敏感性随着合金中的氢含量的增加而增大;在8.5 MPa高温碱性水中,TA16钛合金的应力腐蚀敏感性随着合金中氢含量的增加而增大,但合金中氢的体积浓度小于350 mL/m3时,合金的应力腐蚀敏感指数小于0.2.在8.5 MPa高温碱性水中.TA16钛合金的吸氢量随着浸泡时间的增加而增大,浸泡13 000 h后,TA16钛合金的吸氢体积浓度小于50 mL/m3,合金表面形成的由TiO、TiO2和Ti2O3组成的致密氧化膜.
参考文献
| [1] | Rusli, RH .Role of hydrogen environment induced hydrogen embrittlement of Ti-8Al-1Mo-2V alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):143-146. |
| [2] | Woodtli J.;Kieselbach R. .Damage due to hydrogen embrittlement and stress corrosion cracking[J].Engineering failure analysis,2000(6):427-450. |
| [3] | Song RG;Dietzel W;Zhang BJ;Liu WJ;Tseng MK;Atrens A .Stress corrosion cracking and hydrogen embrittlement of an Al-Zn-Mg-Cu alloy[J].Acta materialia,2004(16):4727-4743. |
| [4] | San-Martin A;Manchester F D .The H-Ti system[J].Bulletin of Alloy Phase Diagrams,1987,8(01):30-42. |
| [5] | 严铿,徐济进,蒋成禹.T225NG钛合金在高温高压水介质中应力腐蚀行为的研究[J].稀有金属,2004(02):425-427. |