对SiC颗粒增强铝基复合材料SiCp/101Al的氩气保护炉中钎焊工艺及机理进行研究.结果表明,通过优化钎焊工艺参数,获得接头的剪切强度最大值可达90 MPa;进一步对钎焊接头进行金相组织观察和钎缝相结构组成分析,钎缝组织致密,未发现有气孔、夹杂和微裂纹等缺陷,钎料和母材之间合金元素存在明显的互扩散,并且母材中有部分SiC颗粒过渡到钎缝之中;接头断口扫描观察显示,接头整体呈现韧性断裂特征.对钎焊接头的强度问题进行讨论.
参考文献
| [1] | 曾汉民.高技术新材料要览[M].北京:中国科学技术出版社,1993:566-569. |
| [2] | 崔岩.碳化硅颗粒增强铝基复合材料的航空航天应用[J].材料工程,2002(06):3-6. |
| [3] | M. B. D. Ellis .Joining of aluminium based metal matrix composites[J].International Materials Reviews,1996(2):41-58. |
| [4] | 林丽华;唐逸民;陈立功 等.碳化硅颗粒增强铝基复合材料SiCp/LD2的钎焊机理[J].焊接学报,1997,18(01):12-17. |
| [5] | Zhang X.P.;Quan G.F.;Wei w. .Preliminary investigation on joining performance of SiC_p-reinforced aluminium metal matrix composite (Al/SiC_p-MMC) by vacuum brazing[J].Composites, Part A. Applied science and manufacturing,1999(6):823-827. |
| [6] | Urefia A;Gil L;Escriche E et al.High temperature soldering of SiC particulate aluminium matrix composites (series 2000)using Zn-Al filler alloys[J].Science and Technology of Welding and Joining,2001,6(01):1-11. |
| [7] | 邹家生,许如强,赵其章.铝基钎料在碳化硅颗粒增强铝基复合材料上的润湿性研究[J].兵器材料科学与工程,2004(02):15-18. |
| [8] | 张启运;庄鸿寿.钎焊手册[M].北京:机械工业出版社,1999:1-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%