研究了添加稀土元素La,Ce(质量百分数依次为0.05%和0.15%)对93WNiFe合金动态性能的影响,所用合金分别为真空处理和锻造退火两种状态.发现添加La,Ce可提高钨合金的动态性能,其原因是W颗粒和粘结相的固熔强化,W颗粒细化,W-M界面净化,W-W界面相对量减少,W在粘结相中溶解度的减小和游离氢的减少.
参考文献
| [1] | RyuHo;JHong et al.Mechanical alloying process of 93W-56Ni-14Fe tungsten heavy alloy[J].Journal of Materials Processing Technology,1997,63(1-3):292-297. |
| [2] | Zhou Guo'an;Liu Yong;Deng Xiu .Interface reaction in liquid-sintering tungsten heavy alloy with Si,Na impurities[J].稀土学报(英文版),1999,17(01):3-9. |
| [3] | 冯庆芬 .稀土元素及后处理工艺对93WNiFe合金动态拉伸性能的影响[D].西安交通大学,1994. |
| [4] | SANGHYUN PARK;DONG-KUK KIM;SUNGHAK LEE .Dynamic Deformation Behavior of an Oxide-Dispersed Tungsten Heavy Alloy Fabricated by Mechanical Alloying[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2001(8):2011-2020. |
| [5] | D.K.Kin;S.Lee .Effect of size and shape of tungsten particles on dynamic torsional properties in tungsten heavy alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1999(5):1261-1273. |
| [6] | 杨超,田时雨.装甲钢动态性能与抗弹性能关系研究[J].兵器材料科学与工程,2002(01):3-7. |
| [7] | 唐长国;朱金华;周惠久 .金属材料屈服强度的应变速率效应和热激活理论[J].金属学报,1995,31(06):248-152. |
| [8] | 唐长国;朱金华;周惠久 .金属材料拉伸的高应变率增塑现象及分析[J].材料研究学报,1996,10(01):16-20. |
| [9] | 唐长国;陈文涛;朱金华 .钨合金高应变率导致的塑性降低及微观机理[J].西安交通大学学报,1997,31(03):28-32. |
| [10] | 唐长国;朱金华;周惠久 .应变率对钨合金抗拉强度及断口形貌的影响[J].稀有金属,1996,20(06):421-424. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%