实验研究了从三价铬镀液中电沉积非晶态Fe-Cr合金镀层,加入适量的NaF能明显减少并细化镀层的微裂纹.XPS分析说明电沉积初始阶段的蓝膜可能为Cr、Fe以及Cr(OH)3、Cr2O3的混合物,而镀层中的Cr、Fe以单质形式存在.XRD表明镀层相结构与镀层的Cr含量有关,镀层非晶态结构的形成可能是Fe晶格畸变和晶粒细化的综合作用.在(NH4)2CO3和H2SO4溶液中的实验表明非晶态Fe-Cr合金镀层的耐蚀性优于晶态Fe-Cr镀层.
参考文献
| [1] | Kawashima A;Asami K;Hashimoto K .An XPS Study of Anodic Behavior of Amorphous Nickel-Phosphorus Alloys containing Chromium, Molybdenum of Tungsten in 1M HCl[J].Corrosion Science,1984,24(09):807-823. |
| [2] | Mcbee C L;Kruger J .Nature of Passive Films on Iron-Chromium Alloys[J].Electrochimica Acta,1972,17(12):1337-1441. |
| [3] | Matsuoka M;Kammel R;Landau U .Electrodeposition of Iron-Chromium-Nickel Alloys[J].Plating and Surface Finishing,1987,74(10):56-60. |
| [4] | 李惠东.从三价铬镀液中电沉积可替代硬铬镀层的铬合金镀层[J].电化学,1998(02):217. |
| [5] | 李松林;李益民;周海晖 等.非晶态Fe-Cr合金镀层的制备[J].表面技术,1999,28(02):9-10. |
| [6] | Tadao Hayashi;Akira Ishihama.Electrodeposition of Chromium-Iron Alloys from Trivalent Chromium Baths[J].Plating and Surface Finishing,1979:36-40. |
| [7] | 李惠东;李敏;李惠琪 .电沉积非晶态铁-铬合金镀层的研究[J].材料保护,1997,30(07):7-9. |
| [8] | 李松林,周海晖,郭鹤桐.Fe-Cr合金镀层结构及非晶化机理探讨[J].材料保护,1999(05):4-5. |
| [9] | Tadao Hayashi;Akira Ishihama .Electrodeposition of Chromium-iron Alloys From Trivalent Chromium Baths[J].Plating and Surface Finishing,1979,66(09):36-40. |
| [10] | 成旦红.电沉积非晶态铁-铬合金镀层的研究[J].电化学,1997(02):202. |
| [11] | C L McBee;J Kruger .Nature of Passive Films on Iron-chromium Alloys[J].Electrochimica Acta,1972,17:1337-1341. |
| [12] | 渡边澈;于维平;李荻.非晶态电镀方法及应用[M].北京:北京航空航天大学出版社,1992 |
| [13] | K Hashimoto;K Osada;T masumoto;S Shimodaira .[J].Corrosion Science,1976,16:71. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%