通过SEM,EDS和XRD研究了Ce对HP40Nb热浸镀铝层组织结构和高温抗氧化性能的影响.结果表明,热浸镀过程中添加质量分数1％Ce促进了镀层外层中Fe2Al5和Fe4Al3Ce相的生成,抑制了内层Fe2Al5相长大；在1 000 ℃/4 h扩散处理过程中,Ce促进了γ向α相的转变以及α相中Ni3Al相的析出,并在渗层内层中生成富Ce相；800C/360 h氧化后,Ce促使渗层外层生成少量Fe2Al5和Cr3Si相,并使渗层外层组织均匀致密；1000℃/360 h氧化后,Ce促使α相长大导致渗层中生成大量的σ相.800℃氧化实验发现1％Ce使渗层组织致密,提高了渗层高温抗氧化性；1 000℃氧化实验发现1％Ce促进了渗层中σ相的生成,阻碍了Al原子的内扩散,保证了氧化过程中渗层表面生成α - Al2O3所需铝含量.
参考文献
| [1] | 喇培清,曾丽,刘致远,王维国,阎峰云,郝远.Al对HP40合金显微组织的影响[J].铸造,2008(05):487-490. |
| [2] | 李处森,杨院生,吴欣强.HP耐热钢结焦、渗碳的原因分析[J].中国腐蚀与防护学报,2002(05):286-289. |
| [3] | 黄志荣.乙烯裂解结焦机理及结焦抑制技术进展[J].江苏石油化工学院学报,2000(02):36-39. |
| [4] | Bril U;Klwer J .Corrosion behavior of high silicon alloys in carbon-bearing and high sulfur atomosphere[J].Materials at High Tempertures,1993,11:151-158. |
| [5] | Klwer J .High temperature corrosion behabiour of iron aluminides and iron-aluminium-chromium alloys[J].Materials and Corrosion,1996,47:685-694. |
| [6] | Kane R H .Effects of silicon and oxidation potential on the earburization of centrifugally cast HK-40[J].Corrosion,1981,37(04):187-199. |
| [7] | 文九巴,胡鹏飞,李晓源.稀土铈对热浸渗铝钢耐高温氧化性能的影响[J].热处理,2005(01):18-21. |
| [8] | 张伟,张战营,徐国辉,文九巴,范志康.稀土对渗铝层/基体界面空洞生长和抗高温剥落性能的影响[J].中国有色金属学报,2005(10):1583-1588. |
| [9] | 张伟,范志康,郭献军,文九巴,张金民.稀土对热浸镀铝钢Al2O3/渗铝层界面空洞生长的影响[J].航空材料学报,2006(02):16-19. |
| [10] | 黄亲国,钟华仁.稀土对热浸镀层组织和性能的影响[J].南昌航空工业学院学报（自然科学版）,1999(02):31-34. |
| [11] | 张伟,刘龙,催新安,文九巴.稀土对镀铝钢扩散层生长影响的研究[J].特种铸造及有色合金,2007(06):472-474. |
| [12] | 于升学,夏原,姚枚.稀土铈对热浸镀铝层组织和性能的影响[J].机械工程材料,2006(06):77-79. |
| [13] | 张伟;郭勤军;文九巴 .稀土在热浸镀铝中行为和分布研究[J].稀土,2009,30(05):51-55. |
| [14] | Shigeaki Kobayashi;Takao Yakou .Control of intermetallic compound layers at interface between steel and aluminum by diffusion-treatment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):44-53. |
| [15] | 余瑞璜 .固体与分子经验电子理论一等效价电子假定[J].科学通报,1981,26(04):204-209. |
| [16] | 刘正;吕振家 .稀土表面处理的空位机制[J].科学通报,1991,36(12):951-954. |
| [17] | Steinfechner K.;Wedemeyer O.;Konys J. .INVESTIGATIONS ON THE TRANSFORMATION BEHAVIOR OF THE INTERMETALLIC PHASE (FE, CR)(2)AL-2 FORMED ON MANET II STEEL BY ALUMINIZING[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,1997(1):33-38. |
| [18] | 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001:37. |
| [19] | C. Stallybrass;G. Sauthoff .Ferritic Fe-Al-Ni-Cr alloys with coherent precipitates for high-temperature applications[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(0):985-990. |
| [20] | F. Lechermann;M. Fahnle;J.M. Sanchez .First-principles investigation of the Ni-Fe-Al system[J].Intermetallics,2005(10):1096-1109. |
| [21] | X. Q. Wu;H. M. Jing;Y. G. Zheng;Z. M. Yao;W. Ke;Z. Q. Hu .The eutectic carbides and creep rupture strength of 25Cr20Ni heat-resistant steel tubes centrifugally cast with different solidification conditions[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):252-260. |
| [22] | Wang CJ;Chen SM .Microstructure and cyclic oxidation behavior of hot dip aluminized coating on Ni-base superalloy Inconel 718[J].Surface & Coatings Technology,2006(7):3862-3866. |
| [23] | 马信清;李美栓 等.弥散CeO2对高温下α-Al2O3氧化膜初期生长的影响[J].金属学报,1995,31(09):399-404. |
| [24] | 马信清.CeO2质点对Al2O3型氧化膜和膜/基体界面的原子结合能的影响[J].材料工程,1995(03):23. |
| [25] | 马信清,彭晓,李美栓,陈全芳,李铁藩.原子结合能测量法研究稀土氧化物对α-Al2O3膜氧化动力学的影响[J].中国有色金属学报,1995(03):73-77,94. |
| [26] | 彭晓.β-NiAl涂层及其加入稀土后的氧化膜表面形貌与生长机制[J].腐蚀科学与防护技术,1997(02):87. |
| [27] | 张伟,陈冬梅.热浸镀镧铝钢的高温耐热行为研究[J].材料工程,2008(07):51-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%