采用X射线衍射和磁性测量等手段研究了金属间化合物La0.85 Ce0.15Fe11.4Si1.6的结构和磁热效应.结果表明,该化合物在211K附近经历了从铁磁到顺磁的二级相变.当外加磁场从OT增加到1.5T时.磁熵变为4.98J/kg·K.通过直接测量的方法得到了La0.85 Ce0.15Fe11.4Si1.6化合物在211K的1.0T～0T退磁场的绝热温变为1.1K.大的熵变值和绝热温变表明La0.85 Ce0.15Fe11.4Si1.6化合物很有潜力作为相应温区的磁制冷材料.
参考文献
| [1] | 胡凤霞 .铁基La(Fe,M)<,13>化合物和Ni-Mn-Ga合金的磁性和磁熵变[D].中国科学院物理研究所,2002. |
| [2] | Feng-xia Hu;Bao-gen Shen;Ji-rong Sun;Zhao-hua Cheng;Guang-hui Rao;Xi-xiang Zhang .Influence of negative lattice expansion and metamagnetic transition on magnetic entropy change in the compound LaFe_(11.4)Si_(1.6)[J].Applied physics letters,2001(23):3675-3677. |
| [3] | Xu Chao;Li Guodong;Wang Ligang .Itinerant-electron metamagnetic transitiun and giant magnetocaloric effect in La0.8Ce0.2Fe11.4Si1.6 compound[J].Journal of Applied Physics,2006,99:12391301-12391303. |
| [4] | Pecharsky VK;Gschneidner KA .Giant magnetocaloric effect in Gd-5(Si2Ge2)[J].Physical review letters,1997(23):4494-4497. |
| [5] | Sun Jirung;Hu Fengxia;Shen Baogen .Comment on "direct measurement of the giant adiabatic temperature change in Gd5 Si2Ge2"[J].Phys Rye Lett,2000,85:4191-4193. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%