采用湿固相机械化学法对氧化铈粉体进行改性处理,考察了改性剂的反应率,机械化学反应时间、煅烧温度、添加剂用量等条件与超细氧化铈粉体的粒度、密度、悬浮性及硬度之间的关系,分析测定了物相和外观形貌.制备了复合超细氧化铈粉体,使常态下基本不发生化学反应的改性剂与被改性的粉体颗粒进行了良好的结合,从而改善了超细氧化铈的性能.
参考文献
| [1] | Ding J;Miao W F;Mccormick P G et al.Mechanoche-mical synthesis of ultrafine Fe powder[J].Applied Physics Letters,1995,67:3804-3806. |
| [2] | Ding J;Tsuzuki T;Mccormick P G .Mechanochemical synthesis of ultrafine ZrO2 powder[J].Nano-Structured Materials,1997,8:75-81. |
| [3] | Dodd A C;Kyaiprasad K;Mccormick P G .Synthesis of ultrafine zirconia powder by mechanochemical processing[J].Scripta Materialia,2001,44:689-694. |
| [4] | Tsuzuki T;Mccormick P G .Mechanochemical synthesis of metal sulphide nanoparticles[J].Nano-Structured Materials,1999,12:75-78. |
| [5] | S.Gopalan;S.C.Singhal .MECHANOCHEMICAL SYNTHESIS OF NANO- SIZED CeO_2[J].Scripta materialia,2000(10):993-996. |
| [6] | Gaffet E;Niepce J-C;Charlot F;Gras CH;Le Caer G;Guichard J-L;Delcroix P;Mocellin A;Tillement O;Bernard F .Some recent developments in mechanical activation and mechanosynthesis[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,1999(1):305-314. |
| [7] | 胡莉茵.沉淀法制备CeO2超微粉末[J].中国稀土学报,1996(04):372. |
| [8] | 黎大兵,胡建东,连建设,张秀燕,陈积伟,郭作兴,王红颖.纳米粉体（CeO2）0.9-x（GdO1.5）x（Sm2O3）0.1的溶胶-凝胶低温燃烧合成[J].硅酸盐学报,2001(04):340-343. |
| [9] | 徐华蕊.用喷雾反应法制备实心球形氧化铈超细粉末[J].稀土,1999(06):29. |
| [10] | 董相廷,李铭,张伟,刘桂霞,洪广言.沉淀法制备CeO2纳米晶与表征[J].中国稀土学报,2001(01):24-26. |
| [11] | 李欢军,李前树.一种制备均匀单分散CeO2纳米微粒的新方法[J].分子科学学报,2000(04):239-241. |
| [12] | 蒋凯,彭程,李五聚,王琳,王鸿燕,梁宏伟,孟健.Ce1-xGdxO2-x/2的溶胶-凝胶法合成及其性质[J].高等学校化学学报,2001(08):1279-1282. |
| [13] | 王成云,苏庆德,钱逸泰.非水溶剂水热法制备CeO2纳米粉[J].化学研究与应用,2001(04):402-405. |
| [14] | 董相廷,麦世坚,张伟,刘桂霞,孙晶,洪元佳,刘景和,洪广言.硬脂酸凝胶法制备CeO2纳米粉体[J].材料科学与工程,2001(01):99-101. |