阐明了碳含量对硬质合金质量控制的重要性以及国内外对用甲烷氢气混合气调整合金碳含量的研究情况.为了在两相区范围内对合金的碳势进行调整,从热力学上估算了不同温度下混合气体浓度的临界值,与试验结果基本符合.优化烧结气氛的试验结果显示:通过选择合适的烧结气氛,对WC-10Co合金性能的提高有明显作用.
参考文献
| [1] | ТвердыеСддαвыСбор .трудовВНИИТС NO[Z].Метадлуртиэдат,1962. |
| [2] | 胡顺遂.碳化钨基硬质合金控碳问题探讨[J].稀有金属与硬质合金,1995(02):14-16. |
| [3] | V P Bondarenko et al.Hydrogen-Containing chemically active gas medium for controlling carbon content of tungsten-base hard alloys[J].International Journal of Hydrogen Energy,1977,22:205-212. |
| [4] | Roy Lueth .[J].Metal Powder Report,1986,7:505. |
| [5] | O Pacher.Influence of vacuum sintering furnace atmosphere on carbon content of hardmetal[J].Powder Metallurgy,1980(04):189-192. |
| [6] | V.P. Bondarenko;S.F. Korablev;I.V. Epik .Optimizing conditions for obtaining a solid solution of tungsten carbide in titanium carbide by preparing it in a precisely controlled gas medium[J].International journal of hydrogen energy,1999(9):845-848. |
| [7] | 吴其山 等.[J].硬质合金,2002,10:47-50. |
| [8] | 王茂青 .气压烧结硬质合金性能的研究[J].硬质合金,1998,11:217-221. |
| [9] | 李学芳 .硬质合金和热动力学模型[J].国外难熔金属和硬质材料,1996,12:6-11. |
| [10] | 谭映国;易丹青 .硬质合金的真空烧结与渗碳反应[J].硬质合金,14:129-133. |
| [11] | 刘永福.硬质合金烧结气氛及其控制[J].硬质合金,1996(08) |
| [12] | 印永嘉;李大珍.物理化学简明教程[M].北京:高等教育出版社,1992:559-567. |
| [13] | 吴冲浒.WC-Co硬质合金磁饱和性能浅论[J].稀有金属与硬质合金,1999(09):45-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%