本文综述了不锈钢晶间腐蚀的各种测试方法(包括化学浸蚀和电化学方法)原理、发展情况及适用范围,可以看出,不锈钢晶间腐蚀试验各方法存在一定的应用范围和优缺点;化学浸蚀法耗时长、且是破坏性的,但应用较成熟,国内外都有对应的参照标准;电化学法快速、无损,易适用于现场检验,在实际试验中应根据试验的目的选用合适的试验方法.
参考文献
| [1] | 魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,1984:156. |
| [2] | 黄畯.电化学动电位再活化法评定不锈钢晶间腐蚀敏感性的研究[J].腐蚀科学与防护技术,1992(04):242. |
| [3] | ASTM A262-2002a.Standard practics for detecting susceptibility to intergranular attack in austenitic stainless steels[S]. |
| [4] | JIS G0572～0575-2000.ステンレス鋼の腐食試験方法[S]. |
| [5] | GB 4334.2～5-2008.金属与合金的腐蚀不锈钢晶间腐蚀试验方法[S]. |
| [6] | Scharfsteln L R;Eisenbrown C M.An evaluation of accelerated strauss testing[A].ASTM,1963:235-239. |
| [7] | Delong W B.Testing multiple specimen of stainless steels in a modified boiling nitric acid test apparatus,symposium on evaluation tests for stainless steels[A].ASTM,1950:211-216. |
| [8] | Warren D .Intergranular Corrosion Resistance of Austenitic Stainless Steels:A Nitric Acid-Hydrofluoric Acid TestASTM Bulletin,No.230[][R].,1958. |
| [9] | GB 4334.4-1984.不锈钢硝酸-氢氟酸腐蚀试验方法[S]. |
| [10] | Streicher M A .Intergranular corrosion resistance of austenitic stainless steels:a ferric sulfate-sulfuric acid test[ASTM Bulletin,No.229][R].,1958. |
| [11] | Streicher M A .Screening stainless steels from the 240-h nitric acid test by electrolytic etching in oxalic Acid[ASTM Bulletin,No.188][R].,1953. |
| [12] | 周纯青,李久青,王志刚.堆焊308L不锈钢晶间腐蚀规律及其电化学检测方法[C].腐蚀科学与防腐蚀工程技术新进展（中国腐蚀与防护学会成立20周年暨'99学术年会：论文专辑）,1999:106-110. |
| [13] | Clerbois L;Clerbois V;Massart J .Intergranular corrosion of austenitic stainless steels (in French:Corrosion intercristalline des aciers inoxydables austenitiques)[J].Electrochimica Acta,1959,1:70-82. |
| [14] | Szklarska-Smialowska S;Cragnolino G .Stress corrosion cracking of sensitized type 304 stainless steel in oxygenated pure water at elevated temperatures(REVIEW)[J].Corrosion,1980,36(12):653-655. |
| [15] | 田昭武.电化学实验方法进展[M].厦门:厦门大学出版社,1988:255-257. |
| [16] | Bruemmer S M;Charlot L A;Arey B W .Sensitization development in austentic stainless steel:correlation between STEM-EDS and EPR Measurements[J].Corrosion,1988,44(06):328-333. |
| [17] | Huang C A;Chang Y Z;Chen S C .The electrochemical behavior of austenitic stainless steel with different degress of sensitization in the transpassive potential region in 1mol/L H2SO4 containing chloride[J].Corrosion Science,2004,46:1501-1513. |
| [18] | 秦丽雁,宋诗哲,卢玉琢.304不锈钢晶间腐蚀过程中的电化学阻抗谱特征[J].中国腐蚀与防护学报,2007(02):74-79. |
| [19] | 方智.电化学动电位再活化法评价308L不锈钢的晶间腐蚀敏感性[J].腐蚀科学与防护技术,1996(02):87. |
| [20] | Fang Z;Wu Y S;Zhang L et al.Application of the modified electrochemical potentiodynamic reactivation method to evaluate intergranular corrosion susceptibility of stainless steel[J].CORROSION,1998,54:339-346. |
| [21] | Matula M;Hyspecka;Svoboda M et al.Intergranular corrosion of AISI 316L steel.mater[J].Charact,2001,46:203-210. |
| [22] | Cihal V;Desestret A;Froment M;Wagner G H.Tests for evaluation of sensibility of stainless steels to intergranular corrosion[A].,1973:249-253. |
| [23] | Cihal V .A potentiokinetic reactivation method for predicting the iCC and iGSCC sensitivity of stainless steels and alloys[J].Corrosion Science,1990,20:737-744. |
| [24] | Cihal V .Advances in the potentiodynamic reactivation method[J].Werkstoffe und Korrosion,1986,37:587-591. |
| [25] | Clarke W L;Carlson D C .Nondestructive measurement of sensitization of stainless steel:relation to high temperature stress corrosion behavior[J].Materials Performance,1980,19(03):16-23. |
| [26] | Majidi A P;Streicher M A .Potentiodynamic reactivation method for detecting sensitization in AISI 304 and 304L stainless steels[J].Corrosion,1984,40(09):393-408. |
| [27] | Katsura R;Kodama M;Nishimura S .DL-EPR study of nentron iradiation in type 304 stainless steel[J].Corrosion,1992,48(05):384-390. |
| [28] | Majidi A P;Streicher M A .Four nondestructive electromechanical tests for decting sensitization in type 304 and 304L stainless steels[J].Nuclear Techonology,1986,75(03):356-369. |
| [29] | P.Muraleedharan .Comparative Study: Degree of Sensitization and Intergranular Stress Corrosion Cracking Susceptibility of Type 304 Stainless Steel[J].Corrosion: The Journal of Science and Engineering,1996(10):790-800. |
| [30] | Vladimir Cihal;Rudolf Stefec .On the development of the electrochemical potentiokinetic method[J].Electrochimica Acta,2001(24/25):3867-3877. |
| [31] | Lee J B .A new electrochemical potentiokinetic reactivation test for determing degree of sensitization in ferritic stainless steel[J].Corrosion,1986,42(02):106-110. |
| [32] | Scully J R;Kelly R G .An electrochemical test for detecting the intergranular corrosion of a duplex stainless steel[J].Corrosion,1986,42(09):537-542. |
| [33] | Frangini S;Mignone A .Modified electrochemical potentiokinetic reactivation method for detecting sensitization in 12wt% Cr ferritic stainless steel[J].Corrosion,1992,48(09):715-726. |
| [34] | Greven O;Buehler H E.Advance in assessing the susceptibility to intergranular corrosion of austenitic stainless steels using the electrochemical reactivation test(ERT)[A]. |
| [35] | 高中平,陈范才,赵常就.EPR法评价晶间腐蚀敏感性的各种判据的比较[J].中国腐蚀与防护学报,2000(04):243-247. |
| [36] | 武晋花.用电化学方法测量不锈钢晶间腐蚀的敏感性[J].冶金标准化与质量,2001(03):12-14. |
| [37] | 陈范才,高中平,胡石林.不锈钢晶间腐蚀检测仪的研制[J].计算机与应用化学,2001(05):433-436,447. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%