用Re-Al-N复合变质剂对M2铸造高速钢进行变质处理,消除了钢中网状共晶碳化物,细化了基体组织,减轻了W、Mo元素偏析,在不降低M2高速钢硬度的情况下,韧性大幅度提高,经1180～1200℃淬火,560℃三次回火后,硬度保持在HRC65～66,冲击韧性由8.5J提高到17.0J.变质处理M2铸造高速钢具有优异的抗热疲劳性能和抗高温磨损性能.
参考文献
| [1] | 郭耕三.高速钢及其热处理[M].北京:机械工业出版社,1985 |
| [2] | Sh. Kheirandish;Sh. Mirdamadi;Y. H. K. Kharrazi .Effect of titanium on cast structure of high speed steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1998(4):312-316. |
| [3] | Boccalini Jr M;Correa A V O;Goldenstein H .Rare earth metal induced modification of r-M2C,r-M6C and r-MC eutectics in as cast M2 high speed steel[J].材料科学与工艺(英文版),1999,15(06):621-626. |
| [4] | Li Yanjun;Jiang Qichuan;Zhao Yuguang et al.Influence of Ti on MC carbide in M2 steel[J].Journal of Materials Science and Technology,1997,13(06):471-474. |
| [5] | 杜挺;韩其勇;王常珍.稀土碱土等元素的物理化学及在材料中的应用[M].北京:科学出版社,1995:64. |
| [6] | Stuchlik J.New progress in wear resistant steels and cast irons[J].Giesserei Praxis,1984(11):167-176. |
| [7] | 郭新成;曾庆梅;束德林 .几种轧辊材料的热磨损和热疲劳性能[J].钢铁,1992,27(11):37-40. |
| [8] | 马臣.Effect of Rare Earth Elements on Thermal Fatigue of High Ni-Cr Alloy Cast Iron[J].JOURNAL OF RARE EARTHS,1996(04):286. |
| [9] | 刘佐民 .M50高速钢高温摩擦磨损特性的研究[J].摩擦学学报,1997,17(01):38-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%