高温高湿条件下对玻璃纤维/碳纤维混杂增强环氧树脂复合材料电缆芯进行加速湿热老化试验,比较了两种直径的复合材料电缆芯在相同老化条件下的力学性能,并从微观角度分析了湿热老化后力学性能下降的原因.结果表明,该复合材料电缆芯耐湿热老化性能较好,在80℃及RH95%下老化1750h后其弯曲强度保留率大于65%,层间剪切强度保留率大于58%.
参考文献
| [1] | 张亚娟,齐暑华.复合材料老化方法研究进展[J].工程塑料应用,2002(01):39-41. |
| [2] | Czigany T .Effect of hygrothermal aging on the fracture and failure behavior in short glass fiber reinforced toughened PBT composites[J].Polymer Composites,1996,17(06):900-902. |
| [3] | Akay M .Moisture absorption and its influence on the tensile properties of glass fiber reinforced polyamide[J].Polymer and Polymer Composite,1994,2(06):349-350. |
| [4] | Michael B .Challenges for composites into the next millennium-a reinforcement perspective[J].Composites Part A:Applied Science and Manufacturing,2001,32:901-903. |
| [5] | Mijovic J;Lin K F .The Effect of hygrothermal fatigue on physical/mechanical properties and morphology of neat epoxy resin and graphite/epoxy composite[J].Journal of Applied Polymer Science,1985,30(06):2527-2549. |
| [6] | 方旭东,杨鸿昌,安章荣.碳纤维/钛超混杂复合材料老化性能研究[J].宇航材料工艺,2002(02):35-37. |
| [7] | 迟倩萍.S2/TDE85复合材料耐自然库存与加速湿热老化的性能研究[J].纤维复合材料,2002(03):32-34. |
| [8] | 冼杏娟;李端义.复合材料破坏分析及微观图谱[M].北京:科学出版社,1993 |
| [9] | 肖迎红,汪信,陆路德,杨绪杰.玻纤增强热塑性聚酯复合材料湿热老化研究[J].工程塑料应用,2001(09):35-37. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%